Properties
General
| Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
|---|---|---|---|---|---|---|
Density | 1.06 g/cm³ Show Supplier Material materials with Density of 1.06 g/cm³ | dry | ISO 1183 | |||
Moisture absorption | 23 °C | 1.6 % Show Supplier Material materials with Moisture absorption of 1.6 % | 50%RH | ISO 62 | 2 mm | |
Water absorption | 5.5 % Show Supplier Material materials with Water absorption of 5.5 % | ISO 62 | 2 mm | immersion at 23°C |
Mechanical
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Elastic modulus | 0.85 GPa Show Supplier Material materials with Elastic modulus of 0.85 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
1.7 GPa Show Supplier Material materials with Elastic modulus of 1.7 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Elongation | 100 % Show Supplier Material materials with Elongation of 100 % | dry, 50%RH | ISO 527-2/1A | min. | 50mm/min | nominal | |
Elongation at yield | 4.5 % Show Supplier Material materials with Elongation at yield of 4.5 % | dry | ISO 527-2/1A | 50mm/min | |
Flexural modulus | 0.75 GPa Show Supplier Material materials with Flexural modulus of 0.75 GPa | 50%RH | ISO 178 | 2mm/min | |
1.6 GPa Show Supplier Material materials with Flexural modulus of 1.6 GPa | dry | ISO 178 | 2mm/min | ||
Flexural strength | 40 MPa Show Supplier Material materials with Flexural strength of 40 MPa | 50%RH | ISO 178 | 2mm/min | |
60 MPa Show Supplier Material materials with Flexural strength of 60 MPa | dry | ISO 178 | 2mm/min | ||
Impact strength, Charpy notched | -30 °C | 25 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 25 kJ/m² | dry | ISO 179/1eA | |
23 °C | 105 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 105 kJ/m² | dry | ISO 179/1eA | ||
23 °C | 120 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 120 kJ/m² | 50%RH | ISO 179/1eA | ||
Yield strength | 35 MPa Show Supplier Material materials with Yield strength of 35 MPa | 50%RH | ISO 527-2/1A | 50mm/min | |
42 MPa Show Supplier Material materials with Yield strength of 42 MPa | dry | ISO 527-2/1A | 50mm/min |
Thermal
| Property | Value | Testing Standard | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature | 55 °C Show Supplier Material materials with Heat deflection temperature of 55 °C | ISO 75/2Af | 1.80 MPa | ||
Melting point | 220 °C Show Supplier Material materials with Melting point of 220 °C | ISO 11357-1/-3 | 10°C/min | ||
Flammability | Thickness tested (mm): 1.6, Class: HB, Standard: UL 94 | Automotive Interior Flammability(mm/min): <30 ,method: ISO 3795 and thickness tested (mm): 3 | ||||
Electrical
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Surface resistivity | 1e+10 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq | 50%RH | IEC 60093 | 500V |
1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | dry | IEC 60093 | 500V | |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | 50%RH | IEC 60093 | 500V |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 60093 | 500V |
Rheological Properties
| Property | Value | Testing Standard | Condition | Comment |
|---|---|---|---|---|
Melt mass-flow rate | 2 g/10min Show Supplier Material materials with Melt mass-flow rate of 2 g/10min | ISO 1133 | 275°C/5Kg | |
Shrinkage | 1.1 % Show Supplier Material materials with Shrinkage of 1.1 % | ISO 294-4 | 280/70/60* | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse |
1.4 % Show Supplier Material materials with Shrinkage of 1.4 % | ISO 294-4 | 280/70/60* | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
Technological properties
| Property | ||
|---|---|---|
| Certifications | RoHS 2011/65/UE | |
| Color | Black | |
| Features | Impact Modified, Heat Stabilized | |
| Processing methods | Injection Molding,Blow Molding | |