RADILON AESTUS T1 RV400RKC 306 BK

Alternative and trade names
PPA-T GF40,PPA-GF40
Want to keep this datasheet? Save it now in your required format

Description

PPA injection moulding grade 40% glass fibre reinforced with high glass transition temperature and high melting point. Black colour.

Suitable for parts requiring high stiffness and strength. High resistance to hot water contact, suitable for drinking water contact.

This material data has been provided by Radici Group.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.52 g/cm³

Show Supplier Material materials with Density of 1.52 g/cm³

ISO 1183, DAM

Water absorption

23.0 °C

0.1 %

Show Supplier Material materials with Water absorption of 0.1 %

ISO 62, thickness tested (mm): 2

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

14.5 GPa

Show Supplier Material materials with Elastic modulus of 14.5 GPa

ISO 527-2/1A, 1mm/min, DAM

Elongation

23.0 °C

2.1 %

Show Supplier Material materials with Elongation of 2.1 %

ISO 527-2/1A, 5mm/min, DAM

Flexural modulus

23.0 °C

13 GPa

Show Supplier Material materials with Flexural modulus of 13 GPa

ISO 178, 2mm/min, DAM

Flexural strength

23.0 °C

330 MPa

Show Supplier Material materials with Flexural strength of 330 MPa

ISO 178, 2mm/min, DAM

Impact strength, Charpy notched

23.0 °C

9.5 - 30 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 9.5 - 30 kJ/m²

ISO 179/1eA

Impact strength, Charpy unnotched

-30.0 °C

60 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 60 kJ/m²

ISO 179/1eU

23.0 °C

65 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 65 kJ/m²

ISO 179/1eU

Tensile strength

23.0 °C

240 MPa

Show Supplier Material materials with Tensile strength of 240 MPa

ISO 527-2/1A, 5mm/min, DAM

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.7E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 1.7E-5 1/K

ISO 11359-1/-2, 23°C-55°C

Coefficient of thermal expansion, transverse

23.0 °C

5.8E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 5.8E-5 1/K

ISO 11359-1/-2, 23°C-55°C

Heat deflection temperature, 1.80 MPa

293 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 293 °C

ISO 75/2Af

Melting point

325 °C

Show Supplier Material materials with Melting point of 325 °C

ISO 11357-1/-3, 10°C/min

Flammability

Class: HB ,method: UL 94, and thickness tested (mm): 0.8

Electrical

PropertyTemperatureValueComment

Surface resistivity

23.0 °C

1.00E+12 Ω/sq

Show Supplier Material materials with Surface resistivity of 1.00E+12 Ω/sq

IEC 60093, 500V, DAM

Volume resistivity

23.0 °C

1.00E+14 Ω·cm

Show Supplier Material materials with Volume resistivity of 1.00E+14 Ω·cm

IEC 60093, 500V, DAM

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.2 %

Show Supplier Material materials with Shrinkage of 0.2 %

ISO 294-4, DAM

Shrinkage, transverse

23.0 °C

0.7 %

Show Supplier Material materials with Shrinkage, transverse of 0.7 %

ISO 294-4, DAM

Technological properties

Property
Certifications

RoHS 2011/65/UE, Food and Water Contact (please get in touch with Radici Group): KTW guidlines and DVGW-standard W270 (11/2007), ACS positive lists include the circular DGC/VS4 n°2000/232 dated 27 april 2000

Color

Black

Fillers

40% Glass Fiber

Processing methods

Injection Molding