RADILON AESTUS T2 RV350W 333 BK

Alternative and trade names
PPA-GF35, PPA-T GF35
Want to keep this datasheet? Save it now in your required format

Description

PPA injection moulding grade 35% glass fibre reinforced with high melting point. Heat stabilized. Black colour.

Suitable for parts requiring high stiffness and strength, intended to work at high temperatures.

This material data has been provided by Radici Group.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionTesting StandardThickness

Density

1.46 g/cm³

Show Supplier Material materials with Density of 1.46 g/cm³

dry

ISO 1183

Water absorption

0.2 %

Show Supplier Material materials with Water absorption of 0.2 %

ISO 62

2 mm

Mechanical

PropertyTemperatureValueConditionTesting StandardComment

Elastic modulus

11 GPa

Show Supplier Material materials with Elastic modulus of 11 GPa

50%RH

ISO 527-2/1A

1mm/min

12 GPa

Show Supplier Material materials with Elastic modulus of 12 GPa

dry

ISO 527-2/1A

1mm/min

Elongation

2 %

Show Supplier Material materials with Elongation of 2 %

dry

ISO 527-2/1A

5mm/min

2 %

Show Supplier Material materials with Elongation of 2 %

50%RH

ISO 527-2/1A

5mm/min

Flexural modulus

10 GPa

Show Supplier Material materials with Flexural modulus of 10 GPa

dry

ISO 178

2mm/min

Flexural strength

285 MPa

Show Supplier Material materials with Flexural strength of 285 MPa

dry

ISO 178

2mm/min

Impact strength, Charpy notched

-30 °C

12 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 12 kJ/m²

dry, 50%RH

ISO 179/1eA

23 °C

12 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 12 kJ/m²

dry

ISO 179/1eA

23 °C

12 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 12 kJ/m²

dry, 50%RH

ISO 179/1eA

Impact strength, Charpy unnotched

-30 °C

46 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 46 kJ/m²

dry

ISO 179/1eU

23 °C

55 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 55 kJ/m²

dry

ISO 179/1eU

Unlock all property charts

Tensile strength

160 MPa

Show Supplier Material materials with Tensile strength of 160 MPa

50%RH

ISO 527-2/1A

5mm/min

185 MPa

Show Supplier Material materials with Tensile strength of 185 MPa

dry

ISO 527-2/1A

5mm/min

Thermal

PropertyValueTesting StandardPressureComment

Coefficient of thermal expansion

1.8e-05 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 1.8e-05 1/K

ISO 11359-1/-2

23°C-55°C

7.3e-05

Show Supplier Material materials with Coefficient of thermal expansion of 7.3e-05

ISO 11359-1/-2

23°C-55°C, Transverse

Heat deflection temperature

280 °C

Show Supplier Material materials with Heat deflection temperature of 280 °C

ISO 75/2Af

2 MPa

Melting point

310 °C

Show Supplier Material materials with Melting point of 310 °C

ISO 11357-1/-3

10°C/min

Flammability

Class: HB ,method: UL 94, and thickness tested (mm): 0.8

Electrical

PropertyValueConditionTesting StandardComment

Volume resistivity

1e+14 Ω·cm

Show Supplier Material materials with Volume resistivity of 1e+14 Ω·cm

dry

IEC 60093

500V

Technological properties

Property
Certifications

RoHS 2011/65/UE

Color

Black

Fillers

35% Glass Fiber

Processing methods

Injection Molding