RADILON D RV600RKC 306 BK

Alternative and trade names
PA610-GF60
Want to keep this datasheet? Save it now in your required format

Description

PA610 60% glass fibre reinforced injection moulding grade. Heat stabilized. Black colour.

Suitable for parts requiring very high stiffness and good mechanical resistance, along with good resistance to hydrolysis. Product specifically intended for applications in civil and industrial water management sector. This grade is partially renewably-sourced (60% of base polymer by weight).

Equivalent Materials

This material data has been provided by Radici Group.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueConditionTesting StandardThicknessComment

Density

1.66 g/cm³

Show Supplier Material materials with Density of 1.66 g/cm³

dry

ISO 1183

Moisture absorption

23 °C

0.5 %

Show Supplier Material materials with Moisture absorption of 0.5 %

50%RH

ISO 62

2 mm

Water absorption

1.3 %

Show Supplier Material materials with Water absorption of 1.3 %

ISO 62

2 mm

immersion at 23°C

Mechanical

PropertyTemperatureValueConditionTesting StandardComment

Elastic modulus

17.2 GPa

Show Supplier Material materials with Elastic modulus of 17.2 GPa

50%RH

ISO 527-2/1A

1mm/min

19 GPa

Show Supplier Material materials with Elastic modulus of 19 GPa

dry

ISO 527-2/1A

1mm/min

Elongation

2.9 %

Show Supplier Material materials with Elongation of 2.9 %

dry

ISO 527-2/1A

5mm/min

3 %

Show Supplier Material materials with Elongation of 3 %

50%RH

ISO 527-2/1A

5mm/min

Flexural modulus

15.4 GPa

Show Supplier Material materials with Flexural modulus of 15.4 GPa

50%RH

ISO 178

2mm/min

17 GPa

Show Supplier Material materials with Flexural modulus of 17 GPa

dry

ISO 178

2mm/min

Flexural strength

320 MPa

Show Supplier Material materials with Flexural strength of 320 MPa

50%RH

ISO 178

2mm/min

340 MPa

Show Supplier Material materials with Flexural strength of 340 MPa

dry

ISO 178

2mm/min

Impact strength, Charpy notched

23 °C

18 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 18 kJ/m²

dry

ISO 179/1eA

Impact strength, Charpy unnotched

23 °C

100 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 100 kJ/m²

dry

ISO 179/1eU

23 °C

105 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 105 kJ/m²

50%RH

ISO 179/1eU

Tensile strength

190 MPa

Show Supplier Material materials with Tensile strength of 190 MPa

50%RH

ISO 527-2/1A

5mm/min

220 MPa

Show Supplier Material materials with Tensile strength of 220 MPa

dry

ISO 527-2/1A

5mm/min

Thermal

PropertyValueTesting StandardComment

Heat deflection temperature

190 °C

Show Supplier Material materials with Heat deflection temperature of 190 °C

ISO 75/2Af

8.00 MPa

215 °C

Show Supplier Material materials with Heat deflection temperature of 215 °C

ISO 75/2Af

1.80 MPa

Melting point

220 °C

Show Supplier Material materials with Melting point of 220 °C

ISO 11357-1/-3

10°C/min

Vicat softening temperature

215 °C

Show Supplier Material materials with Vicat softening temperature of 215 °C

ISO 306

1.00E+12mm

Flammability

Thickness tested (mm): 3, Class: HB, Standard: UL 94

Electrical

PropertyValueConditionTesting StandardComment

Surface resistivity

1e+12 Ω/sq

Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq

dry

IEC 60093

500V

Volume resistivity

1e+11 Ω·cm

Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm

50%RH

IEC 60093

500V

1e+13 Ω·cm

Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm

dry

IEC 60093

500V

Rheological Properties

PropertyValueConditionTesting StandardComment

Shrinkage

0.2 %

Show Supplier Material materials with Shrinkage of 0.2 %

280/90/60*

ISO 294-4

*Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa]

0.3 %

Show Supplier Material materials with Shrinkage of 0.3 %

280/90/60*

ISO 294-4

*Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse

Technological properties

Property
Additives

Release agent

Certifications

RoHS 2011/65/UE

Color

Black

Fillers

60% Glass Fiber

Processing methods

Injection Molding