RADILON A RV350HHR 3800 BK

Alternative and trade names
PA66-T GF35, PA66-GF35
Want to keep this datasheet? Save it now in your required format

Description

PA66 35% glass fibre reinforced injection moulding grade with enhanced thermal resistance in contact with hot air. High improvement of mechanical properties retention versus standard polyamide 66 after heat ageing.

Alternative to PPA and PA4.6 grades in automotive applications like turbo air ducts, CAC tanks, EGR housing. Continuous use temperature until 210 °C in air.

This material data has been provided by Radici Group.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.39 g/cm³

Show Supplier Material materials with Density of 1.39 g/cm³

ISO 1183, DAM

Moisture absorption

23.0 °C

1.5 %

Show Supplier Material materials with Moisture absorption of 1.5 %

ISO 62, 50% RH, thickness tested (mm): 2

Water absorption

23.0 °C

6.3 %

Show Supplier Material materials with Water absorption of 6.3 %

ISO 62, thickness tested (mm): 2

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

10.5 GPa

Show Supplier Material materials with Elastic modulus of 10.5 GPa

ISO 527-2/1A, 1mm/min, DAM

Elongation

23.0 °C

3.5 %

Show Supplier Material materials with Elongation of 3.5 %

ISO 527-2/1A, 5mm/min, DAM

Flexural modulus

23.0 °C

9.4 GPa

Show Supplier Material materials with Flexural modulus of 9.4 GPa

ISO 178, 2mm/min, DAM

Flexural strength

23.0 °C

265 MPa

Show Supplier Material materials with Flexural strength of 265 MPa

ISO 178, 2mm/min, DAM

Impact strength, Charpy notched

23.0 °C

14 - 30 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 14 - 30 kJ/m²

ISO 179/1eA

Impact strength, Charpy unnotched

-30.0 °C

95 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 95 kJ/m²

ISO 179/1eU

23.0 °C

95 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 95 kJ/m²

ISO 179/1eU

Tensile strength

23.0 °C

170 MPa

Show Supplier Material materials with Tensile strength of 170 MPa

ISO 527-2/1A, 5mm/min, DAM

Thermal

PropertyValueComment

Ball pressure temperature

160 °C

Show Supplier Material materials with Ball pressure temperature of 160 °C

IEC 60695-10-2

Heat deflection temperature, 1.80 MPa

240 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 240 °C

ISO 75/2Af

Melting point

260 °C

Show Supplier Material materials with Melting point of 260 °C

ISO 11357-1/-3, 10°C/min

Flammability

Class: HB ,method: UL 94

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

350 V

Show Supplier Material materials with Comparative tracking index of 350 V

IEC 60112, Sol.A, DAM

Surface resistivity

23.0 °C

1.00E+12 Ω/sq

Show Supplier Material materials with Surface resistivity of 1.00E+12 Ω/sq

IEC 60093, 500V, DAM

Volume resistivity

23.0 °C

1.00E+14 Ω·cm

Show Supplier Material materials with Volume resistivity of 1.00E+14 Ω·cm

IEC 60093, 500V, DAM

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.4 %

Show Supplier Material materials with Shrinkage of 0.4 %

ISO 294-4, DAM

Shrinkage, transverse

23.0 °C

0.9 %

Show Supplier Material materials with Shrinkage, transverse of 0.9 %

ISO 294-4, DAM

Technological properties

Property
Certifications

RoHS 2011/65/UE

Fillers

35% Glass Fiber

Processing methods

Injection Molding