RADIFLAM AESTUS T2 RV300 HF 100 NT

Alternative and trade names
PA6T/66-GF30 FR(40)
Want to keep this datasheet? Save it now in your required format

Description

PPA flame retardant injection moulding grade, 30% glass fibre reinforced. Halogen and red phosphorus free. High melting point. Natural colour.

Suitable for parts requiring fire retardancy along with high stiffness and good mechanical resistance. Suitable for Lead Free Soldering application. Rated V0 according to UL94.

Equivalent Materials

This material data has been provided by Radici Group.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueConditionTesting StandardThicknessComment

Density

1.47 g/cm³

Show Supplier Material materials with Density of 1.47 g/cm³

dry

ISO 1183

Moisture absorption

23 °C

1.3 %

Show Supplier Material materials with Moisture absorption of 1.3 %

50%RH

ISO 62

2 mm

Water absorption

0.1 %

Show Supplier Material materials with Water absorption of 0.1 %

ISO 62

2 mm

24h immersion at 23°C

Mechanical

PropertyTemperatureValueConditionTesting StandardComment

Elastic modulus

10.9 GPa

Show Supplier Material materials with Elastic modulus of 10.9 GPa

dry

ISO 527-2/1A

1mm/min

11 GPa

Show Supplier Material materials with Elastic modulus of 11 GPa

50%RH

ISO 527-2/1A

1mm/min

Elongation

2.2 %

Show Supplier Material materials with Elongation of 2.2 %

50%RH

ISO 527-2/1A

5mm/min

2.4 %

Show Supplier Material materials with Elongation of 2.4 %

dry

ISO 527-2/1A

5mm/min

Flexural modulus

11 GPa

Show Supplier Material materials with Flexural modulus of 11 GPa

dry

ISO 178

2mm/min

Flexural strength

240 MPa

Show Supplier Material materials with Flexural strength of 240 MPa

dry

ISO 178

2mm/min

Impact strength, Charpy notched

23 °C

10 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 10 kJ/m²

dry

ISO 179/1eA

23 °C

11 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 11 kJ/m²

50%RH

ISO 179/1eA

Impact strength, Charpy unnotched

-30 °C

50 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 50 kJ/m²

dry

ISO 179/1eU

23 °C

55 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 55 kJ/m²

dry

ISO 179/1eU

Tensile strength

135 MPa

Show Supplier Material materials with Tensile strength of 135 MPa

50%RH

ISO 527-2/1A

5mm/min

155 MPa

Show Supplier Material materials with Tensile strength of 155 MPa

dry

ISO 527-2/1A

5mm/min

Thermal

PropertyValueThicknessTesting StandardComment

Glow Wire Flammability Index

960 °C

Show Supplier Material materials with Glow Wire Flammability Index of 960 °C

1 mm, 2 mm

IEC 60695-2-12

Glow Wire Ignition Temperature

800 °C

Show Supplier Material materials with Glow Wire Ignition Temperature of 800 °C

1 mm, 2 mm

IEC 60695-2-13

Heat deflection temperature

280 °C

Show Supplier Material materials with Heat deflection temperature of 280 °C

ISO 75/2Af

1.80 MPa

Melting point

305 °C

Show Supplier Material materials with Melting point of 305 °C

ISO 11357-1/-3

10°C/min

Flammability

Thickness tested (mm): 0.4, Class: V-0, Standard: UL 94 | Thickness tested (mm): 1.5, Class: 5VA, Standard: UL 94 | Thickness tested (mm): 1.5, Class: 5VA, Standard: IEC 60695-11-20 at dry condition (Burning behaviour)

Electrical

PropertyValueConditionTesting StandardComment

Comparative tracking index

600 V

Show Supplier Material materials with Comparative tracking index of 600 V

dry

IEC 60112

Sol.A

Dielectric strength

42 kV/mm

Show Supplier Material materials with Dielectric strength of 42 kV/mm

dry

IEC 60243-1

44 kV/mm

Show Supplier Material materials with Dielectric strength of 44 kV/mm

50%RH

IEC 60243-1

Surface resistivity

1e+12 Ω/sq

Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq

dry

IEC 60093

500V

Volume resistivity

1e+13 Ω·cm

Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm

dry

IEC 60093

500V

Rheological Properties

PropertyValueConditionTesting StandardComment

Shrinkage

0.4 %

Show Supplier Material materials with Shrinkage of 0.4 %

315/120/60*

ISO 294-4

*Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa]

0.9 %

Show Supplier Material materials with Shrinkage of 0.9 %

315/120/60*

ISO 294-4

*Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse

Technological properties

Property
Additives

Release agent, Flame retarding agent

Certifications

Yellow Card, RoHS 2011/65/UE

Color

Natural

Features

Flame Retardant, Heat Stabilized

Fillers

30% Glass Fiber

Processing methods

Injection Molding