RADILON A RV300RKC 106 NT

Alternative and trade names
PA66-GF30
Want to keep this datasheet? Save it now in your required format

Description

PA66 30% glass fibre reinforced injection moulding grade. Heat stabilized. Natural colour.

Suitable for parts requiring high stiffness and good mechanical resistance. Good resistance to hydrolysis. Product specifically intended for applications in civil and industrial water management sector. Suitable and approved for drinking water and foodstuff contact.

This material data has been provided by Radici Group.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionTesting StandardThickness

Density

1.36 g/cm³

Show Supplier Material materials with Density of 1.36 g/cm³

dry

ISO 1183

Moisture absorption

1.6 %

Show Supplier Material materials with Moisture absorption of 1.6 %

50% RH

ISO 62

2 mm

Water absorption

6.2 %

Show Supplier Material materials with Water absorption of 6.2 %

ISO 62

2 mm

Mechanical

PropertyTemperatureValueConditionTesting StandardComment

Elastic modulus

8 GPa

Show Supplier Material materials with Elastic modulus of 8 GPa

50%RH

ISO 527-2/1A

1mm/min

10 GPa

Show Supplier Material materials with Elastic modulus of 10 GPa

dry

ISO 527-2/1A

1mm/min

Elongation

4 %

Show Supplier Material materials with Elongation of 4 %

dry

ISO 527-2/1A

5mm/min

6 %

Show Supplier Material materials with Elongation of 6 %

50%RH

ISO 527-2/1A

5mm/min

Flexural modulus

6 GPa

Show Supplier Material materials with Flexural modulus of 6 GPa

50%RH

ISO 178

2mm/min

9 GPa

Show Supplier Material materials with Flexural modulus of 9 GPa

dry

ISO 178

2mm/min

Flexural strength

220 MPa

Show Supplier Material materials with Flexural strength of 220 MPa

50%RH

ISO 178

2mm/min

290 MPa

Show Supplier Material materials with Flexural strength of 290 MPa

dry

ISO 178

2mm/min

Impact strength, Charpy notched

-30 °C

11 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 11 kJ/m²

dry

ISO 179/1eA

23 °C

15 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 15 kJ/m²

dry

ISO 179/1eA

23 °C

18 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 18 kJ/m²

50%RH

ISO 179/1eA

Impact strength, Charpy unnotched

-30 °C

75 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 75 kJ/m²

dry

ISO 179/1eU

23 °C

95 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 95 kJ/m²

dry

ISO 179/1eU

23 °C

105 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 105 kJ/m²

50%RH

ISO 179/1eU

Unlock all property charts

Tensile strength

140 MPa

Show Supplier Material materials with Tensile strength of 140 MPa

50%RH

ISO 527-2/1A

5mm/min

193 MPa

Show Supplier Material materials with Tensile strength of 193 MPa

dry

ISO 527-2/1A

5mm/min

Thermal

PropertyValueThicknessTesting StandardPressureComment

Glow Wire Flammability Index

700 °C

Show Supplier Material materials with Glow Wire Flammability Index of 700 °C

2 mm

IEC 60695-2-12

Heat deflection temperature

245 °C

Show Supplier Material materials with Heat deflection temperature of 245 °C

ISO 75/2Af

2 MPa

255 °C

Show Supplier Material materials with Heat deflection temperature of 255 °C

ISO 75/2Bf

0.45 MPa

Melting point

260 °C

Show Supplier Material materials with Melting point of 260 °C

ISO 11357-1/-3

10°C/min

Vicat softening temperature

250 °C

Show Supplier Material materials with Vicat softening temperature of 250 °C

ISO 306

50°C/h 50N

Flammability

Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3 | Class: HB ,method: UL 94, and thickness tested (mm): 0.8

Electrical

PropertyValueConditionTesting StandardComment

Comparative tracking index

550 V

Show Supplier Material materials with Comparative tracking index of 550 V

dry

IEC 60112

Sol.A

Surface resistivity

1e+10 Ω/sq

Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq

50%RH

IEC 60093

500V

1e+12 Ω/sq

Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq

dry

IEC 60093

500V

Volume resistivity

1e+12 Ω·cm

Show Supplier Material materials with Volume resistivity of 1e+12 Ω·cm

50%RH

IEC 60093

500V

1e+14 Ω·cm

Show Supplier Material materials with Volume resistivity of 1e+14 Ω·cm

dry

IEC 60093

500V

Rheological Properties

PropertyValueConditionTesting StandardComment

Shrinkage

0.3 %

Show Supplier Material materials with Shrinkage of 0.3 %

dry

ISO 294-4

1 %

Show Supplier Material materials with Shrinkage of 1 %

dry

ISO 294-4

Transverse

Technological properties

Property
Certifications

RoHS 2011/65/UE, Food and Water Contact (please get in touch with Radici Group): KTW guidlines and DVGW-standard W270 (11/2007), ACS positive lists include the circular DGC/VS4 n°2000/232 dated 27 april 2000

Color

Natural

Fillers

30% Glass Fiber

Processing methods

Injection Molding