Properties
General
| Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
|---|---|---|---|---|---|---|
Density | 1.33 g/cm³ Show Supplier Material materials with Density of 1.33 g/cm³ | dry | ISO 1183 | |||
Moisture absorption | 23 °C | 1 % Show Supplier Material materials with Moisture absorption of 1 % | 50%RH | ISO 62 | 2 mm | |
Water absorption | 2.2 % Show Supplier Material materials with Water absorption of 2.2 % | ISO 62 | 2 mm | immersion at 23°C |
Mechanical
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Elastic modulus | 6.8 GPa Show Supplier Material materials with Elastic modulus of 6.8 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
8.5 GPa Show Supplier Material materials with Elastic modulus of 8.5 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Elongation | 4.5 % Show Supplier Material materials with Elongation of 4.5 % | dry | ISO 527-2/1A | 5mm/min | |
6 % Show Supplier Material materials with Elongation of 6 % | 50%RH | ISO 527-2/1A | 5mm/min | ||
Flexural modulus | 5.9 GPa Show Supplier Material materials with Flexural modulus of 5.9 GPa | 50%RH | ISO 178 | 2mm/min | |
7.6 GPa Show Supplier Material materials with Flexural modulus of 7.6 GPa | dry | ISO 178 | 2mm/min | ||
Flexural strength | 190 MPa Show Supplier Material materials with Flexural strength of 190 MPa | 50%RH | ISO 178 | 2mm/min | |
235 MPa Show Supplier Material materials with Flexural strength of 235 MPa | dry | ISO 178 | 2mm/min | ||
Impact strength, Charpy notched | 23 °C | 15 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 15 kJ/m² | dry | ISO 179/1eA | |
23 °C | 17 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 17 kJ/m² | 50%RH | ISO 179/1eA | ||
Impact strength, Charpy unnotched | 23 °C | 100 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 100 kJ/m² | dry | ISO 179/1eU | |
23 °C | 105 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 105 kJ/m² | 50%RH | ISO 179/1eU | ||
Tensile strength | 120 MPa Show Supplier Material materials with Tensile strength of 120 MPa | 50%RH | ISO 527-2/1A | 5mm/min | |
150 MPa Show Supplier Material materials with Tensile strength of 150 MPa | dry | ISO 527-2/1A | 5mm/min |
Thermal
| Property | Value | Testing Standard | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature | 200 °C Show Supplier Material materials with Heat deflection temperature of 200 °C | ISO 75/2Af | 1.80 MPa | ||
Melting point | 220 °C Show Supplier Material materials with Melting point of 220 °C | ISO 11357-1/-3 | 10°C/min | ||
Flammability | Thickness tested (mm): 0.8, Class: HB, Standard: UL 94 | ||||
Rheological Properties
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Shrinkage | 0.4 % Show Supplier Material materials with Shrinkage of 0.4 % | 280/80/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
0.8 % Show Supplier Material materials with Shrinkage of 0.8 % | 280/80/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse |
Technological properties
| Property | ||
|---|---|---|
| Additives | Release agent | |
| Certifications | RoHS 2011/65/UE | |
| Color | Black | |
| Features | Heat Stabilized | |
| Fillers | 30% Glass Fiber | |
| Processing methods | Injection Molding | |