Properties
General
| Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
|---|---|---|---|---|---|---|
Density | 1.17 g/cm³ Show Supplier Material materials with Density of 1.17 g/cm³ | dry | ISO 1183 | |||
Limiting oxygen index | 23 °C | 35 % Show Supplier Material materials with Limiting oxygen index of 35 % | ISO 4589-2 | |||
Moisture absorption | 23 °C | 1.8 % Show Supplier Material materials with Moisture absorption of 1.8 % | 50%RH | ISO 62 | 2 mm | |
Specific optical density | 35 [-] Show Supplier Material materials with Specific optical density of 35 [-] | EN ISO 5659-2 | ||||
Water absorption | 7.7 % Show Supplier Material materials with Water absorption of 7.7 % | ISO 62 | 2 mm | immersion at 23°C |
Mechanical
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Elastic modulus | 2.6 GPa Show Supplier Material materials with Elastic modulus of 2.6 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
3.5 GPa Show Supplier Material materials with Elastic modulus of 3.5 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Elongation | 12 % Show Supplier Material materials with Elongation of 12 % | dry | ISO 527-2/1A | 50mm/min | nominal | |
50 % Show Supplier Material materials with Elongation of 50 % | 50%RH | ISO 527-2/1A | 50mm/min | nominal | ||
Flexural modulus | 3.3 GPa Show Supplier Material materials with Flexural modulus of 3.3 GPa | dry | ISO 178 | 2mm/min | |
Flexural strength | 110 MPa Show Supplier Material materials with Flexural strength of 110 MPa | dry | ISO 178 | 2mm/min | |
Impact strength, Charpy notched | -30 °C | 4 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 4 kJ/m² | dry | ISO 179/1eA | |
23 °C | 4.5 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 4.5 kJ/m² | dry | ISO 179/1eA | ||
23 °C | 6.5 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 6.5 kJ/m² | 50%RH | ISO 179/1eA | ||
Impact strength, Charpy unnotched | 23 °C | 75 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 75 kJ/m² | dry | ISO 179/1eU | |
23 °C | 120 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 120 kJ/m² | 50%RH | ISO 179/1eU | ||
Yield strength | 50 MPa Show Supplier Material materials with Yield strength of 50 MPa | 50%RH | ISO 527-2/1A | 50mm/min | |
75 MPa Show Supplier Material materials with Yield strength of 75 MPa | dry | ISO 527-2/1A | 50mm/min |
Thermal
| Property | Value | Thickness | Testing Standard | Comment | |||
|---|---|---|---|---|---|---|---|
Glow Wire Flammability Index | 960 °C Show Supplier Material materials with Glow Wire Flammability Index of 960 °C | 1 mm | IEC 60695-2-12 | ||||
Glow Wire Ignition Temperature | 750 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 750 °C | 2 mm | IEC 60695-2-13 | ||||
775 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 775 °C | 1 mm | IEC 60695-2-13 | |||||
Heat deflection temperature | 70 °C Show Supplier Material materials with Heat deflection temperature of 70 °C | ISO 75/2Af | 1.80 MPa | ||||
200 °C Show Supplier Material materials with Heat deflection temperature of 200 °C | ISO 75/2Bf | 0.45 MPa | |||||
Melting point | 260 °C Show Supplier Material materials with Melting point of 260 °C | ISO 11357-1/-3 | 10°C/min | ||||
Time-temperature limit | 121 °C Show Supplier Material materials with Time-temperature limit of 121 °C | ISO 2578 | 20000h | at 50% loss of Tensile Strength | ||||
134 °C Show Supplier Material materials with Time-temperature limit of 134 °C | ISO 2578 | 20000h | at 50% loss of Dielectric Strength | |||||
151 °C Show Supplier Material materials with Time-temperature limit of 151 °C | ISO 2578 | 5000h | at 50% loss of Tensile Strength | |||||
186 °C Show Supplier Material materials with Time-temperature limit of 186 °C | ISO 2578 | 5000h | at 50% loss of Dielectric Strength | |||||
Vicat softening temperature | 220 °C Show Supplier Material materials with Vicat softening temperature of 220 °C | ISO 306 | 50°C/h 50N | ||||
Flammability | Thickness tested (mm): 0.4 and 0.8, Class: V-0, Standard: UL 94 | Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3 | ||||||
Electrical
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Comparative tracking index | 600 V Show Supplier Material materials with Comparative tracking index of 600 V | dry | IEC 60112 | Sol.A |
Dielectric strength | 26 kV/mm Show Supplier Material materials with Dielectric strength of 26 kV/mm | 50%RH | IEC 60243-1 | |
31 kV/mm Show Supplier Material materials with Dielectric strength of 31 kV/mm | dry | IEC 60243-1 | ||
Surface resistivity | 1e+10 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq | 50%RH | IEC 60093 | 500V |
1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | dry | IEC 60093 | 500V | |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | 50%RH | IEC 60093 | 500V |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 60093 | 500V |
Rheological Properties
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Shrinkage | 1.1 % Show Supplier Material materials with Shrinkage of 1.1 % | 280/70/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
1.1 % Show Supplier Material materials with Shrinkage of 1.1 % | 280/70/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse |
Technological properties
| Property | ||
|---|---|---|
| Additives | Release agent, Flame retarding agent | |
| Certifications | Yellow Card, RoHS 2011/65/UE | |
| Color | Natural | |
| Features | Flame Retardant, Heat Stabilized | |
| Other | Fire Classification I2/F2, Standard: NF F16-101 R23/HL3, Standard: EN 45545-2 0.45 for thickness 1mm according to NF X70-100-1/2 | |
| Processing methods | Injection Molding | |