RADIFLAM A FRX 308 BK

Alternative and trade names
PA66 FR(30)

Want to keep this datasheet? Save it now in your required format

Description

PA66 flame retardant injection moulding grade with enhanced mechanical properties retention after thermal aging. Halogen and phosphorus free. Black colour.

Suitable for parts where fire retardancy is required. Rated V-0 at 0.25 mm according to UL-94.

Equivalent Materials

PA66

This material data has been provided by Radici Group.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

RADICIGROUP HIGH PERFORMANCE POLYMERS

MANUFACTURER

Additional services:

CAE Service: Customized technical support contributing to the success of innovative projects, including metal replacement applications, realized using RADILON®, RADITECK®, RADISTRONG®, RADIFLAM® and RADITER® engineering plastics. This is what RadiciGroup High Performance Polymers can offer its customers, thanks to its state-of-the-art computer-aided engineering (CAE) virtual simulation tools and the experience of its technical specialists.

Materials by this supplier

RADILON A CP300K 333 BK

RADILON AESTUS T1 RV300FC 306K BK

TORZEN Marathon G3500XHL BK20

RADILON NeXTreme RV500HHR 3800 BK

RADITER B RV300 100 NT

See all materials by this supplier

Use cases

Webinar: Metal Replacement with Engineering Polymers

Properties

General

Property	Temperature	Value	Condition	Testing Standard	Thickness	Comment
Density		1.18 g/cm³ Show Supplier Material materials with Density of 1.18 g/cm³	dry	ISO 1183
Limiting oxygen index	23 °C	32 % Show Supplier Material materials with Limiting oxygen index of 32 %		ISO 4589-2
Moisture absorption	23 °C	1.8 % Show Supplier Material materials with Moisture absorption of 1.8 %	50%RH	ISO 62	2 mm
Water absorption		7.7 % Show Supplier Material materials with Water absorption of 7.7 %		ISO 62	2 mm	immersion at 23°C

Mechanical

Property	Temperature	Value	Condition	Testing Standard	Comment
Elastic modulus		3.6 GPa Show Supplier Material materials with Elastic modulus of 3.6 GPa	dry	ISO 527-2/1A	1mm/min
Elongation		5.5 % Show Supplier Material materials with Elongation of 5.5 %	dry	ISO 527-2/1A	50mm/min \| nominal
Flexural modulus		3.5 GPa Show Supplier Material materials with Flexural modulus of 3.5 GPa	dry	ISO 178	2mm/min
Flexural strength		115 MPa Show Supplier Material materials with Flexural strength of 115 MPa	dry	ISO 178	2mm/min
Impact strength, Charpy notched	23 °C	4.5 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 4.5 kJ/m²	dry	ISO 179/1eA
Impact strength, Charpy unnotched	23 °C	30 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 30 kJ/m²	dry	ISO 179/1eU
Yield strength		75 MPa Show Supplier Material materials with Yield strength of 75 MPa	dry	ISO 527-2/1A	50mm/min

Thermal

Property	Value	Testing Standard	Thickness	Comment
Ball pressure temperature	200 °C Show Supplier Material materials with Ball pressure temperature of 200 °C	IEC 60695-10-2
Glow Wire Flammability Index	960 °C Show Supplier Material materials with Glow Wire Flammability Index of 960 °C	IEC 60695-2-12	1 mm
Glow Wire Ignition Temperature	725 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 725 °C	IEC 60695-2-13	2 mm
	800 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 800 °C	IEC 60695-2-13	1 mm
Heat deflection temperature	70 °C Show Supplier Material materials with Heat deflection temperature of 70 °C	ISO 75/2Af		1.80 MPa
	200 °C Show Supplier Material materials with Heat deflection temperature of 200 °C	ISO 75/2Bf		0.45 MPa
Melting point	260 °C Show Supplier Material materials with Melting point of 260 °C	ISO 11357-1/-3		10°C/min
Vicat softening temperature	220 °C Show Supplier Material materials with Vicat softening temperature of 220 °C	ISO 306		50°C/h 50N
Flammability	Thickness tested (mm): 0.4 and 0.2, Class: V-0, Standard: UL 94 \| Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3

Electrical

Property	Value	Condition	Testing Standard	Comment
Comparative tracking index	600 V Show Supplier Material materials with Comparative tracking index of 600 V	dry	IEC 60112	Sol.A
Surface resistivity	1e+10 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq	50%RH	IEC 60093	500V
	1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq	dry	IEC 60093	500V
Volume resistivity	1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm	50%RH	IEC 60093	500V
	1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm	dry	IEC 60093	500V

Rheological Properties

Property	Value	Condition	Testing Standard	Comment
Shrinkage	1.1 % Show Supplier Material materials with Shrinkage of 1.1 %	280/70/60*	ISO 294-4	*Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa]
	1.1 % Show Supplier Material materials with Shrinkage of 1.1 %	280/70/60*	ISO 294-4	*Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse

Technological properties

Property
Additives	Release agent, Flame retarding agent
Certifications	Yellow Card, RoHS 2011/65/UE
Color	Black
Features	Flame Retardant, Halogen-free, Heat Stabilized
Processing methods	Injection Molding