Properties
General
| Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
|---|---|---|---|---|---|---|
Density | 1.47 g/cm³ Show Supplier Material materials with Density of 1.47 g/cm³ | dry | ISO 1183 | |||
Moisture absorption | 23 °C | 1.3 % Show Supplier Material materials with Moisture absorption of 1.3 % | 50%RH | ISO 62 | 2 mm | |
Water absorption | 5.4 % Show Supplier Material materials with Water absorption of 5.4 % | ISO 62 | 2 mm | immersion at 23°C |
Mechanical
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Elastic modulus | 10.1 GPa Show Supplier Material materials with Elastic modulus of 10.1 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
11.8 GPa Show Supplier Material materials with Elastic modulus of 11.8 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Elongation | 2.3 % Show Supplier Material materials with Elongation of 2.3 % | dry | ISO 527-2/1A | 5mm/min | |
2.5 % Show Supplier Material materials with Elongation of 2.5 % | 50%RH | ISO 527-2/1A | 5mm/min | ||
Flexural modulus | 10.2 GPa Show Supplier Material materials with Flexural modulus of 10.2 GPa | 50%RH | ISO 178 | 2mm/min | |
12.2 GPa Show Supplier Material materials with Flexural modulus of 12.2 GPa | dry | ISO 178 | 2mm/min | ||
Flexural strength | 180 MPa Show Supplier Material materials with Flexural strength of 180 MPa | 50%RH | ISO 178 | 2mm/min | |
230 MPa Show Supplier Material materials with Flexural strength of 230 MPa | dry | ISO 178 | 2mm/min | ||
Impact strength, Charpy notched | -30 °C | 9 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 9 kJ/m² | dry | ISO 179/1eA | |
23 °C | 10 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 10 kJ/m² | dry | ISO 179/1eA | ||
23 °C | 14 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 14 kJ/m² | 50%RH | ISO 179/1eA | ||
Impact strength, Charpy unnotched | -30 °C | 65 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 65 kJ/m² | dry | ISO 179/1eU | |
23 °C | 70 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 70 kJ/m² | dry | ISO 179/1eU | ||
23 °C | 75 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 75 kJ/m² | 50%RH | ISO 179/1eU | ||
Tensile strength | 110 MPa Show Supplier Material materials with Tensile strength of 110 MPa | 50%RH | ISO 527-2/1A | 5mm/min | |
145 MPa Show Supplier Material materials with Tensile strength of 145 MPa | dry | ISO 527-2/1A | 5mm/min |
Thermal
| Property | Value | Thickness | Testing Standard | Comment | |||
|---|---|---|---|---|---|---|---|
Glow Wire Flammability Index | 960 °C Show Supplier Material materials with Glow Wire Flammability Index of 960 °C | 1 mm, 2 mm | IEC 60695-2-12 | ||||
Glow Wire Ignition Temperature | 750 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 750 °C | 1 mm | IEC 60695-2-13 | ||||
775 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 775 °C | 2 mm | IEC 60695-2-13 | |||||
Heat deflection temperature | 245 °C Show Supplier Material materials with Heat deflection temperature of 245 °C | ISO 75/2Af | 1.80 MPa | ||||
260 °C Show Supplier Material materials with Heat deflection temperature of 260 °C | ISO 75/2Bf | 0.45 MPa | |||||
Melting point | 260 °C Show Supplier Material materials with Melting point of 260 °C | ISO 11357-1/-3 | 10°C/min | ||||
Vicat softening temperature | 250 °C Show Supplier Material materials with Vicat softening temperature of 250 °C | ISO 306 | 50°C/h 50N | ||||
Flammability | Thickness tested (mm): 0.8, Class: V-0, Standard: UL 94 | Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3 | ||||||
Electrical
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Comparative tracking index | 600 V Show Supplier Material materials with Comparative tracking index of 600 V | dry | IEC 60112 | Sol.A |
Surface resistivity | 1e+10 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq | 50%RH | IEC 60093 | 500V |
1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | dry | IEC 60093 | 500V | |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | 50%RH | IEC 60093 | 500V |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 60093 | 500V |
Rheological Properties
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Shrinkage | 0.3 % Show Supplier Material materials with Shrinkage of 0.3 % | 280/80/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
0.9 % Show Supplier Material materials with Shrinkage of 0.9 % | 280/80/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse |
Technological properties
| Property | ||
|---|---|---|
| Additives | Release agent, Flame retarding agent | |
| Certifications | Yellow Card, RoHS 2011/65/UE | |
| Color | Natural | |
| Features | Flame Retardant, Heat Stabilized | |
| Fillers | 35% Glass Fiber | |
| Processing methods | Injection Molding | |