Properties
General
| Property | Value | Testing Standard |
|---|---|---|
Density | 1.67 g/cm³ Show Supplier Material materials with Density of 1.67 g/cm³ | ISO 1183 |
Mechanical
| Property | Temperature | Value | Testing Standard | Comment |
|---|---|---|---|---|
Elastic modulus | 10.6 GPa Show Supplier Material materials with Elastic modulus of 10.6 GPa | ISO 527-2/1A | 1mm/min | |
Elongation | 2.5 % Show Supplier Material materials with Elongation of 2.5 % | ISO 527-2/1A | 5mm/min | |
Flexural modulus | 10.1 GPa Show Supplier Material materials with Flexural modulus of 10.1 GPa | ISO 178 | 2mm/min | |
Flexural strength | 210 MPa Show Supplier Material materials with Flexural strength of 210 MPa | ISO 178 | 2mm/min | |
Impact strength, Charpy notched | 23 °C | 10 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 10 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | 23 °C | 60 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 60 kJ/m² | ISO 179/1eU | |
Tensile strength | 135 MPa Show Supplier Material materials with Tensile strength of 135 MPa | ISO 527-2/1A | 5mm/min |
Thermal
| Property | Value | Thickness | Testing Standard | Comment | |||
|---|---|---|---|---|---|---|---|
Glow Wire Flammability Index | 960 °C Show Supplier Material materials with Glow Wire Flammability Index of 960 °C | 1 mm, 2 mm | IEC 60695-2-12 | ||||
Heat deflection temperature | 205 °C Show Supplier Material materials with Heat deflection temperature of 205 °C | ISO 75/2Af | 1.80 MPa | ||||
220 °C Show Supplier Material materials with Heat deflection temperature of 220 °C | ISO 75/2Bf | 0.45 MPa | |||||
Melting point | 225 °C Show Supplier Material materials with Melting point of 225 °C | ISO 11357-1/-3 | 10°C/min | ||||
Vicat softening temperature | 210 °C Show Supplier Material materials with Vicat softening temperature of 210 °C | ISO 306 | 50°C/h 50N | ||||
Flammability | Thickness tested (mm): 0.4 and 0.8, Class: V-0, Standard: UL 94 | Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3 | ||||||
Electrical
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Comparative tracking index | 250 V Show Supplier Material materials with Comparative tracking index of 250 V | IEC 60112 | Sol.A |
Surface resistivity | 1e+10 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq | IEC 60093 | 500V |
1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | IEC 60093 | 500V | |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | IEC 60093 | 500V |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | IEC 60093 | 500V |
Rheological Properties
| Property | Value | Testing Standard | Condition | Comment |
|---|---|---|---|---|
Melt mass-flow rate | 3.5 g/10min Show Supplier Material materials with Melt mass-flow rate of 3.5 g/10min | ISO 1133 | 250°C/2.16Kg | |
Shrinkage | 0.4 % Show Supplier Material materials with Shrinkage of 0.4 % | ISO 294-4 | 270/80/60* | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
0.9 % Show Supplier Material materials with Shrinkage of 0.9 % | ISO 294-4 | 270/80/60* | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse |
Technological properties
| Property | ||
|---|---|---|
| Additives | Release agent, Flame retarding agent | |
| Certifications | Yellow Card, RoHS 2011/65/UE | |
| Color | Black | |
| Features | Flame Retardant, Heat Stabilized | |
| Fillers | 30% Glass Fiber | |
| Processing methods | Injection Molding | |