General
Property | Value | Testing Standard |
---|---|---|
Density | 1.44 g/cm³ Show Supplier Material materials with Density of 1.44 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Testing Standard | Comment |
---|---|---|---|---|
Elastic modulus | 2.9 GPa Show Supplier Material materials with Elastic modulus of 2.9 GPa | ISO 527-2/1A | 1mm/min | |
Elongation | 2.7 % Show Supplier Material materials with Elongation of 2.7 % | ISO 527-2/1A | 5mm/min | |
Flexural modulus | 2.5 GPa Show Supplier Material materials with Flexural modulus of 2.5 GPa | ISO 178 | 2mm/min | |
Flexural strength | 90 MPa Show Supplier Material materials with Flexural strength of 90 MPa | ISO 178 | 2mm/min | |
Impact strength, Charpy notched | 23 °C | 2.8 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 2.8 kJ/m² | ISO 179/1eA | |
Tensile strength | 55 MPa Show Supplier Material materials with Tensile strength of 55 MPa | ISO 527-2/1A | 5mm/min |
Thermal
Property | Value | Testing Standard | Comment | ||
---|---|---|---|---|---|
Melting point | 225 °C Show Supplier Material materials with Melting point of 225 °C | ISO 11357-1/-3 | 10°C/min | ||
Flammability | Thickness tested (mm): 0.8, Class: V-0, Standard: UL 94 |
Rheological Properties
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Shrinkage | 1.9 % Show Supplier Material materials with Shrinkage of 1.9 % | 260/60/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
1.9 % Show Supplier Material materials with Shrinkage of 1.9 % | 260/60/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse |
Technological properties
Property | ||
---|---|---|
Additives | Release agent, Flame retarding agent | |
Certifications | Yellow Card, RoHS 2011/65/UE | |
Color | Black | |
Features | Flame Retardant, Heat Stabilized | |
Processing methods | Injection Molding |