General
Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
---|---|---|---|---|---|---|
Density | 1.77 g/cm³ Show Supplier Material materials with Density of 1.77 g/cm³ | dry | ISO 1183 | |||
Limiting oxygen index | 23 °C | 45 % Show Supplier Material materials with Limiting oxygen index of 45 % | ISO 4589-2 | |||
Moisture absorption | 23 °C | 1.1 % Show Supplier Material materials with Moisture absorption of 1.1 % | 50%RH | ISO 62 | 2 mm | |
Water absorption | 2.5 % Show Supplier Material materials with Water absorption of 2.5 % | ISO 62 | 2 mm | immersion at 23°C |
Mechanical
Property | Temperature | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|---|
Elastic modulus | 14.8 GPa Show Supplier Material materials with Elastic modulus of 14.8 GPa | dry | ISO 527-2/1A | 1mm/min | |
Elongation | 1.9 % Show Supplier Material materials with Elongation of 1.9 % | dry | ISO 527-2/1A | 5mm/min | |
Flexural modulus | 15.4 GPa Show Supplier Material materials with Flexural modulus of 15.4 GPa | dry | ISO 178 | 2mm/min | |
Flexural strength | 245 MPa Show Supplier Material materials with Flexural strength of 245 MPa | dry | ISO 178 | 2mm/min | |
Impact strength, Charpy unnotched | 23 °C | 50 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 50 kJ/m² | dry | ISO 179/1eU | |
Tensile strength | 150 MPa Show Supplier Material materials with Tensile strength of 150 MPa | dry | ISO 527-2/1A | 5mm/min |
Thermal
Property | Value | Thickness | Testing Standard | Comment | |||
---|---|---|---|---|---|---|---|
Glow Wire Flammability Index | 960 °C Show Supplier Material materials with Glow Wire Flammability Index of 960 °C | 1 mm, 2 mm | IEC 60695-2-12 | ||||
Glow Wire Ignition Temperature | 725 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 725 °C | 1 mm, 2 mm | IEC 60695-2-13 | ||||
Heat deflection temperature | 200 °C Show Supplier Material materials with Heat deflection temperature of 200 °C | ISO 75/2Af | 1.80 MPa | ||||
215 °C Show Supplier Material materials with Heat deflection temperature of 215 °C | ISO 75/2Bf | 0.45 MPa | |||||
Melting point | 220 °C Show Supplier Material materials with Melting point of 220 °C | ISO 11357-1/-3 | 10°C/min | ||||
Vicat softening temperature | 205 °C Show Supplier Material materials with Vicat softening temperature of 205 °C | ISO 306 | 50°C/h 50N | ||||
Flammability | Thickness tested (mm): 1.6, Class: V-0, Standard: UL 94 | Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3 |
Electrical
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Comparative tracking index | 600 V Show Supplier Material materials with Comparative tracking index of 600 V | dry | IEC 60112 | Sol.A |
Surface resistivity | 1e+10 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq | 50%RH | IEC 60093 | 500V |
1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | dry | IEC 60093 | 500V | |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | 50%RH | IEC 60093 | 500V |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 60093 | 500V |
Technological properties
Property | ||
---|---|---|
Additives | Release agent, Flame retarding agent | |
Certifications | Yellow Card, RoHS 2011/65/UE | |
Color | Natural | |
Features | Flame Retardant, Heat Stabilized | |
Fillers | 25% Glass Fiber | |
Processing methods | Injection Molding |