General
Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
---|---|---|---|---|---|---|
Density | 1.32 g/cm³ Show Supplier Material materials with Density of 1.32 g/cm³ | dry | ISO 1183 | |||
Moisture absorption | 23 °C | 2 % Show Supplier Material materials with Moisture absorption of 2 % | 50%RH | ISO 62 | 2 mm | |
Water absorption | 7.4 % Show Supplier Material materials with Water absorption of 7.4 % | ISO 62 | 2 mm | immersion at 23°C |
Mechanical
Property | Temperature | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|---|
Elastic modulus | 5.8 GPa Show Supplier Material materials with Elastic modulus of 5.8 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
8 GPa Show Supplier Material materials with Elastic modulus of 8 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Elongation | 3.8 % Show Supplier Material materials with Elongation of 3.8 % | dry | ISO 527-2/1A | 5mm/min | |
6 % Show Supplier Material materials with Elongation of 6 % | 50%RH | ISO 527-2/1A | 5mm/min | ||
Flexural modulus | 4.2 GPa Show Supplier Material materials with Flexural modulus of 4.2 GPa | 50%RH | ISO 178 | 2mm/min | |
7.2 GPa Show Supplier Material materials with Flexural modulus of 7.2 GPa | dry | ISO 178 | 2mm/min | ||
Flexural strength | 155 MPa Show Supplier Material materials with Flexural strength of 155 MPa | 50%RH | ISO 178 | 2mm/min | |
250 MPa Show Supplier Material materials with Flexural strength of 250 MPa | dry | ISO 178 | 2mm/min | ||
Impact strength, Charpy notched | -30 °C | 9 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 9 kJ/m² | dry | ISO 179/1eA | |
23 °C | 11 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 11 kJ/m² | dry | ISO 179/1eA | ||
23 °C | 13 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 13 kJ/m² | 50%RH | ISO 179/1eA | ||
Impact strength, Charpy unnotched | -30 °C | 55 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 55 kJ/m² | dry | ISO 179/1eU | |
23 °C | 65 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 65 kJ/m² | dry | ISO 179/1eU | ||
23 °C | 80 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 80 kJ/m² | 50%RH | ISO 179/1eU | ||
Impact strength, Izod notched | 23 °C | 9.7 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 9.7 kJ/m² | dry | ISO 180/1A | |
23 °C | 12 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 12 kJ/m² | 50%RH | ISO 180/1A | ||
Tensile strength | 115 MPa Show Supplier Material materials with Tensile strength of 115 MPa | 50%RH | ISO 527-2/1A | 5mm/min | |
170 MPa Show Supplier Material materials with Tensile strength of 170 MPa | dry | ISO 527-2/1A | 5mm/min |
Thermal
Property | Value | Thickness | Testing Standard | Comment | |||
---|---|---|---|---|---|---|---|
Glow Wire Flammability Index | 650 °C Show Supplier Material materials with Glow Wire Flammability Index of 650 °C | 1 mm | IEC 60695-2-12 | ||||
675 °C Show Supplier Material materials with Glow Wire Flammability Index of 675 °C | 2 mm | IEC 60695-2-12 | |||||
Glow Wire Ignition Temperature | 675 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 675 °C | 1 mm | IEC 60695-2-13 | ||||
700 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 700 °C | 2 mm | IEC 60695-2-13 | |||||
Heat deflection temperature | 230 °C Show Supplier Material materials with Heat deflection temperature of 230 °C | ISO 75/2Af | 1.80 MPa | ||||
250 °C Show Supplier Material materials with Heat deflection temperature of 250 °C | ISO 75/2Bf | 0.45 MPa | |||||
Melting point | 260 °C Show Supplier Material materials with Melting point of 260 °C | ISO 11357-1/-3 | 10°C/min | ||||
Time-temperature limit | 140 °C Show Supplier Material materials with Time-temperature limit of 140 °C | ISO 2578 | 20000h | at 50% loss of Tensile Strength | ||||
170 °C Show Supplier Material materials with Time-temperature limit of 170 °C | ISO 2578 | 5000h | at 50% loss of Tensile Strength | |||||
Vicat softening temperature | 250 °C Show Supplier Material materials with Vicat softening temperature of 250 °C | ISO 306 | 1.00E+12mm | ||||
Flammability | Thickness tested (mm): 2.45, Class: HB, Standard: UL 94 | Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3 |
Electrical
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Comparative tracking index | 600 V Show Supplier Material materials with Comparative tracking index of 600 V | dry | IEC 60112 | Sol.A |
Surface resistivity | 1e+10 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq | 50%RH | IEC 60093 | 500V |
1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | dry | IEC 60093 | 500V | |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | 50%RH | IEC 60093 | 500V |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 60093 | 500V |
Rheological Properties
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Shrinkage | 0.4 % Show Supplier Material materials with Shrinkage of 0.4 % | 300/90/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
1 % Show Supplier Material materials with Shrinkage of 1 % | 300/90/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse | |
Viscosity number | 130 cm³/gr Show Supplier Material materials with Viscosity number of 130 cm³/gr | ISO 307 | Sulfuric acid |
Technological properties
Property | ||
---|---|---|
Additives | Release agent | |
Certifications | RoHS 2011/65/UE | |
Color | Natural brown | |
Features | Heat Stabilized | |
Fillers | 25% Glass Fiber | |
Processing methods | Injection Molding |