General
Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
---|---|---|---|---|---|---|
Density | 1.13 g/cm³ Show Supplier Material materials with Density of 1.13 g/cm³ | dry | ISO 1183 | |||
Moisture absorption | 23 °C | 0.7 % Show Supplier Material materials with Moisture absorption of 0.7 % | 50%RH | ISO 62 | 2 mm | |
Water absorption | 1.5 % Show Supplier Material materials with Water absorption of 1.5 % | ISO 62 | 2 mm | immersion at 23°C |
Mechanical
Property | Temperature | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|---|
Elastic modulus | 0.68 GPa Show Supplier Material materials with Elastic modulus of 0.68 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
1.1 GPa Show Supplier Material materials with Elastic modulus of 1.1 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Elongation | 70 % Show Supplier Material materials with Elongation of 70 % | dry | ISO 527-2/1A | 50mm/min | nominal | |
100 % Show Supplier Material materials with Elongation of 100 % | 50%RH | ISO 527-2/1A | min. | 50mm/min | nominal | ||
Elongation at yield | 40 % Show Supplier Material materials with Elongation at yield of 40 % | dry | ISO 527-2/1A | 50mm/min | |
Flexural modulus | 1.1 GPa Show Supplier Material materials with Flexural modulus of 1.1 GPa | dry | ISO 178 | 2mm/min | |
Flexural strength | 34 MPa Show Supplier Material materials with Flexural strength of 34 MPa | dry | ISO 178 | 2mm/min | |
Impact strength, Charpy notched | 23 °C | 70 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 70 kJ/m² | dry | ISO 179/1eA | |
Yield strength | 28 MPa Show Supplier Material materials with Yield strength of 28 MPa | 50%RH | ISO 527-2/1A | 50mm/min | |
38 MPa Show Supplier Material materials with Yield strength of 38 MPa | dry | ISO 527-2/1A | 50mm/min |
Thermal
Property | Value | Testing Standard | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 0.000168 1/K Show Supplier Material materials with Coefficient of thermal expansion of 0.000168 1/K | ISO 11359-1/-2 | 23°C-55°C | ||
0.000169 1/K Show Supplier Material materials with Coefficient of thermal expansion of 0.000169 1/K | ISO 11359-1/-2 | 23°C-55°C, Transverse | |||
Heat deflection temperature | 50 °C Show Supplier Material materials with Heat deflection temperature of 50 °C | ISO 75/2Af | 1.80 MPa | ||
Melting point | 217 °C Show Supplier Material materials with Melting point of 217 °C | ISO 11357-1/-3 | 10°C/min | ||
Flammability | Thickness tested (mm): 0.8, Class: HB, Standard: UL 94 | Automotive Interior Flammability(mm/min): <30 ,method: ISO 3795 and thickness tested (mm): 3 |
Electrical
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Surface resistivity | 100000 Ω/sq Show Supplier Material materials with Surface resistivity of 100000 Ω/sq | dry, 50%RH | IEC 60093 | 500V |
Volume resistivity | 1e+07 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+07 Ω·cm | dry, 50%RH | IEC 60093 | 500V |
Technological properties
Property | ||
---|---|---|
Additives | Plasticizer | |
Certifications | RoHS 2011/65/UE | |
Color | Black | |
Features | Eletrically Dissipative, Increased Electrical Conductivity, Anti-Static Modified, Impact Modified, Heat Stabilized | |
Processing methods | Injection Molding,Profile Extrusion |