General
Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
---|---|---|---|---|---|---|
Density | 1.26 g/cm³ Show Supplier Material materials with Density of 1.26 g/cm³ | dry | ISO 1183 | |||
Moisture absorption | 23 °C | 1 % Show Supplier Material materials with Moisture absorption of 1 % | 50%RH | ISO 62 | 2 mm | |
Water absorption | 2.2 % Show Supplier Material materials with Water absorption of 2.2 % | ISO 62 | 2 mm | immersion at 23°C |
Mechanical
Property | Temperature | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|---|
Elastic modulus | 5.1 GPa Show Supplier Material materials with Elastic modulus of 5.1 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
7 GPa Show Supplier Material materials with Elastic modulus of 7 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Elongation | 5 % Show Supplier Material materials with Elongation of 5 % | dry | ISO 527-2/1A | 5mm/min | |
8 % Show Supplier Material materials with Elongation of 8 % | 50%RH | ISO 527-2/1A | 5mm/min | ||
Flexural modulus | 4.5 GPa Show Supplier Material materials with Flexural modulus of 4.5 GPa | 50%RH | ISO 178 | 2mm/min | |
6.2 GPa Show Supplier Material materials with Flexural modulus of 6.2 GPa | dry | ISO 178 | 2mm/min | ||
Flexural strength | 140 MPa Show Supplier Material materials with Flexural strength of 140 MPa | 50%RH | ISO 178 | 2mm/min | |
180 MPa Show Supplier Material materials with Flexural strength of 180 MPa | dry | ISO 178 | 2mm/min | ||
Impact strength, Charpy notched | -30 °C | 20 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 20 kJ/m² | dry | ISO 179/1eA | |
23 °C | 30 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 30 kJ/m² | dry | ISO 179/1eA | ||
23 °C | 40 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 40 kJ/m² | 50%RH | ISO 179/1eA | ||
Impact strength, Charpy unnotched | -30 °C | 85 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 85 kJ/m² | dry | ISO 179/1eU | |
23 °C | 100 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 100 kJ/m² | dry | ISO 179/1eU | ||
23 °C | 105 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 105 kJ/m² | 50%RH | ISO 179/1eU | ||
Tensile strength | 90 MPa Show Supplier Material materials with Tensile strength of 90 MPa | 50%RH | ISO 527-2/1A | 5mm/min | |
115 MPa Show Supplier Material materials with Tensile strength of 115 MPa | dry | ISO 527-2/1A | 5mm/min |
Thermal
Property | Value | Testing Standard | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature | 195 °C Show Supplier Material materials with Heat deflection temperature of 195 °C | ISO 75/2Af | 1.80 MPa | ||
Melting point | 220 °C Show Supplier Material materials with Melting point of 220 °C | ISO 11357-1/-3 | 10°C/min | ||
Flammability | Thickness tested (mm): 0.8, Class: HB, Standard: UL 94 |
Technological properties
Property | ||
---|---|---|
Additives | Release agent | |
Certifications | RoHS 2011/65/UE | |
Color | Black | |
Features | Impact Modified, Heat Stabilized | |
Fillers | 30% Glass Fiber | |
Processing methods | Injection Molding |