Properties
General
| Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
|---|---|---|---|---|---|---|
Density | 1.13 g/cm³ Show Supplier Material materials with Density of 1.13 g/cm³ | dry | ISO 1183 | |||
Moisture absorption | 23 °C | 3.1 % Show Supplier Material materials with Moisture absorption of 3.1 % | 50%RH | ISO 62 | 2 mm | |
Water absorption | 11 % Show Supplier Material materials with Water absorption of 11 % | ISO 62 | 2 mm | immersion at 23°C |
Mechanical
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Elastic modulus | 2.7 GPa Show Supplier Material materials with Elastic modulus of 2.7 GPa | dry | ISO 527-2/1A | 1mm/min | |
Elongation | 50 % Show Supplier Material materials with Elongation of 50 % | dry | ISO 527-2/1A | min. | 50mm/min | nominal | |
Elongation at yield | 4.3 % Show Supplier Material materials with Elongation at yield of 4.3 % | dry | ISO 527-2/1A | 50mm/min | |
Flexural modulus | 2.6 GPa Show Supplier Material materials with Flexural modulus of 2.6 GPa | dry | ISO 178 | 2mm/min | |
Flexural strength | 100 MPa Show Supplier Material materials with Flexural strength of 100 MPa | dry | ISO 178 | 2mm/min | |
Impact strength, Charpy notched | 23 °C | 7.5 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 7.5 kJ/m² | dry | ISO 179/1eA | |
Yield strength | 75 MPa Show Supplier Material materials with Yield strength of 75 MPa | dry | ISO 527-2/1A | 50mm/min |
Thermal
| Property | Value | Testing Standard | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature | 60 °C Show Supplier Material materials with Heat deflection temperature of 60 °C | ISO 75/2Af | 1.80 MPa | ||
170 °C Show Supplier Material materials with Heat deflection temperature of 170 °C | ISO 75/2Bf | 0.45 MPa | |||
Melting point | 220 °C Show Supplier Material materials with Melting point of 220 °C | ISO 11357-1/-3 | 10°C/min | ||
Vicat softening temperature | 200 °C Show Supplier Material materials with Vicat softening temperature of 200 °C | ISO 306 | 50°C/h 50N | ||
Flammability | Thickness tested (mm): 0.8, Class: HB, Standard: UL 94 | Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3 | ||||
Electrical
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Surface resistivity | 1e+10 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq | 50%RH | IEC 60093 | 500V |
1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | dry | IEC 60093 | 500V | |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | 50%RH | IEC 60093 | 500V |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 60093 | 500V |
Rheological Properties
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Shrinkage | 0.8 % Show Supplier Material materials with Shrinkage of 0.8 % | 280/60/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
0.9 % Show Supplier Material materials with Shrinkage of 0.9 % | 280/60/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse | |
Viscosity number | 245 cm³/gr Show Supplier Material materials with Viscosity number of 245 cm³/gr | ISO 307 | Sulfuric acid |
Technological properties
| Property | ||
|---|---|---|
| Certifications | RoHS 2011/65/UE | |
| Color | Natural | |
| Features | Heat Stabilized | |
| Processing methods | Injection Molding,Profile Extrusion | |