Properties
General
| Property | Value | Condition | Testing Standard |
|---|---|---|---|
Density | 1.14 g/cm³ Show Supplier Material materials with Density of 1.14 g/cm³ | dry | ISO 1183 |
Mechanical
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Elastic modulus | 3.1 GPa Show Supplier Material materials with Elastic modulus of 3.1 GPa | dry | ISO 527-2/1A | 1mm/min | |
Elongation | 20 % Show Supplier Material materials with Elongation of 20 % | dry | ISO 527-2/1A | 50mm/min | nominal | |
Elongation at yield | 4.2 % Show Supplier Material materials with Elongation at yield of 4.2 % | dry | ISO 527-2/1A | 50mm/min | |
Flexural modulus | 3.0 GPa Show Supplier Material materials with Flexural modulus of 3.0 GPa | dry | ISO 178 | 2mm/min | |
Flexural strength | 105 MPa Show Supplier Material materials with Flexural strength of 105 MPa | dry | ISO 178 | 2mm/min | |
Impact strength, Charpy notched | -30 °C | 4 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 4 kJ/m² | dry | ISO 179/1eA | |
23 °C | 5 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 5 kJ/m² | dry | ISO 179/1eA | ||
Yield strength | 75 MPa Show Supplier Material materials with Yield strength of 75 MPa | dry | ISO 527-2/1A | 50mm/min |
Thermal
| Property | Value | Thickness | Testing Standard | Comment | |||
|---|---|---|---|---|---|---|---|
Glow Wire Flammability Index | 650 °C Show Supplier Material materials with Glow Wire Flammability Index of 650 °C | 2 mm | IEC 60695-2-12 | ||||
Heat deflection temperature | 70 °C Show Supplier Material materials with Heat deflection temperature of 70 °C | ISO 75/2Af | 1.80 MPa | ||||
Melting point | 220 °C Show Supplier Material materials with Melting point of 220 °C | ISO 11357-1/-3 | 10°C/min | ||||
Vicat softening temperature | 200 °C Show Supplier Material materials with Vicat softening temperature of 200 °C | ISO 306 | 50°C/h 50N | ||||
Flammability | Thickness tested (mm): 0.8, Class: HB, Standard: UL 94 | Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3 | ||||||
Electrical
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Surface resistivity | 1e+10 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq | 50%RH | IEC 60093 | 500V |
1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | dry | IEC 60093 | 500V | |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | 50%RH | IEC 60093 | 500V |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 60093 | 500V |
Rheological Properties
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Shrinkage | 0.9 % Show Supplier Material materials with Shrinkage of 0.9 % | 270/70/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
0.9 % Show Supplier Material materials with Shrinkage of 0.9 % | 270/70/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse |
Technological properties
| Property | ||
|---|---|---|
| Additives | Release agent | |
| Certifications | RoHS 2011/65/UE | |
| Color | Natural grey | |
| Features | Low Friction | |
| Processing methods | Injection Molding | |