RADILON S CT300L 9139 GY

Alternative and trade names
PA6-MD30

Want to keep this datasheet? Save it now in your required format

Description

PA6 30% mineral filled injection moulding grade. Lubricated. Grey colour.

Suitable for parts requiring good dimensional stability, reduced shrinkage and low warpage.

Equivalent Materials

PA6-MD30

This material data has been provided by Radici Group.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

RADICIGROUP HIGH PERFORMANCE POLYMERS

MANUFACTURER

Additional services:

CAE Service: Customized technical support contributing to the success of innovative projects, including metal replacement applications, realized using RADILON®, RADITECK®, RADISTRONG®, RADIFLAM® and RADITER® engineering plastics. This is what RadiciGroup High Performance Polymers can offer its customers, thanks to its state-of-the-art computer-aided engineering (CAE) virtual simulation tools and the experience of its technical specialists.

Materials by this supplier

RADILON A CP300K 333 BK

RADILON AESTUS T1 RV300FC 306K BK

TORZEN Marathon G3500XHL BK20

RADILON NeXTreme RV500HHR 3800 BK

RADITER B RV300 100 NT

See all materials by this supplier

Use cases

Webinar: Metal Replacement with Engineering Polymers

Properties

General

Property	Value	Condition	Testing Standard
Density	1.38 g/cm³ Show Supplier Material materials with Density of 1.38 g/cm³	dry	ISO 1183

Mechanical

Property	Temperature	Value	Condition	Testing Standard	Comment
Elastic modulus		3.5 GPa Show Supplier Material materials with Elastic modulus of 3.5 GPa	50%RH	ISO 527-2/1A	1mm/min
		6.9 GPa Show Supplier Material materials with Elastic modulus of 6.9 GPa	dry	ISO 527-2/1A	1mm/min
Elongation		3.6 % Show Supplier Material materials with Elongation of 3.6 %	dry	ISO 527-2/1A	5mm/min
		12 % Show Supplier Material materials with Elongation of 12 %	50%RH	ISO 527-2/1A	5mm/min
Flexural modulus		3.4 GPa Show Supplier Material materials with Flexural modulus of 3.4 GPa	50%RH	ISO 178	2mm/min
		6.8 GPa Show Supplier Material materials with Flexural modulus of 6.8 GPa	dry	ISO 178	2mm/min
Flexural strength		70 MPa Show Supplier Material materials with Flexural strength of 70 MPa	50%RH	ISO 178	2mm/min
		115 MPa Show Supplier Material materials with Flexural strength of 115 MPa	dry	ISO 178	2mm/min
Impact strength, Charpy notched	23 °C	3.5 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 3.5 kJ/m²	dry	ISO 179/1eA
	23 °C	5 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 5 kJ/m²	50%RH	ISO 179/1eA
Tensile strength		35 MPa Show Supplier Material materials with Tensile strength of 35 MPa	50%RH	ISO 527-2/1A	5mm/min
		65 MPa Show Supplier Material materials with Tensile strength of 65 MPa	dry	ISO 527-2/1A	5mm/min

Thermal

Property	Value	Testing Standard	Comment
Heat deflection temperature	95 °C Show Supplier Material materials with Heat deflection temperature of 95 °C	ISO 75/2Af	1.80 MPa
	195 °C Show Supplier Material materials with Heat deflection temperature of 195 °C	ISO 75/2Bf	0.45 MPa
Melting point	220 °C Show Supplier Material materials with Melting point of 220 °C	ISO 11357-1/-3	10°C/min
Vicat softening temperature	205 °C Show Supplier Material materials with Vicat softening temperature of 205 °C	ISO 306	50°C/h 50N
Flammability	Thickness tested (mm): 1.6, Class: HB, Standard: UL 94 \| Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3

Electrical

Property	Value	Condition	Testing Standard	Comment
Surface resistivity	1e+10 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq	50%RH	IEC 60093	500V
	1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq	dry	IEC 60093	500V
Volume resistivity	1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm	50%RH	IEC 60093	500V
	1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm	dry	IEC 60093	500V

Rheological Properties

Property	Value	Testing Standard	Condition	Comment
Melt mass-flow rate	25 g/10min Show Supplier Material materials with Melt mass-flow rate of 25 g/10min	ISO 1133		250°C/2.16Kg
Shrinkage	0.7 % Show Supplier Material materials with Shrinkage of 0.7 %	ISO 294-4	280/80/60*	*Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa]
	0.8 % Show Supplier Material materials with Shrinkage of 0.8 %	ISO 294-4	280/80/60*	*Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse

Technological properties

Property
Additives	Release agent
Certifications	RoHS 2011/65/UE
Color	Grey colour
Fillers	30% Mineral Powder
Processing methods	Injection Molding