General
Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
---|---|---|---|---|---|---|
Density | 1.56 g/cm³ Show Supplier Material materials with Density of 1.56 g/cm³ | dry | ISO 1183 | |||
Moisture absorption | 23 °C | 1.4 % Show Supplier Material materials with Moisture absorption of 1.4 % | 50%RH | ISO 62 | 2 mm | |
Water absorption | 4.8 % Show Supplier Material materials with Water absorption of 4.8 % | ISO 62 | 2 mm | immersion at 23°C |
Mechanical
Property | Temperature | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|---|
Elastic modulus | 9.8 GPa Show Supplier Material materials with Elastic modulus of 9.8 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
16.8 GPa Show Supplier Material materials with Elastic modulus of 16.8 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Elongation | 3 % Show Supplier Material materials with Elongation of 3 % | dry | ISO 527-2/1A | 5mm/min | |
6 % Show Supplier Material materials with Elongation of 6 % | 50%RH | ISO 527-2/1A | 5mm/min | ||
Flexural modulus | 8.7 GPa Show Supplier Material materials with Flexural modulus of 8.7 GPa | 50%RH | ISO 178 | 2mm/min | |
15.1 GPa Show Supplier Material materials with Flexural modulus of 15.1 GPa | dry | ISO 178 | 2mm/min | ||
Flexural strength | 190 MPa Show Supplier Material materials with Flexural strength of 190 MPa | 50%RH | ISO 178 | 2mm/min | |
350 MPa Show Supplier Material materials with Flexural strength of 350 MPa | dry | ISO 178 | 2mm/min | ||
Impact strength, Charpy notched | -30 °C | 14 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 14 kJ/m² | dry | ISO 179/1eA | |
-30 °C | 18 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 18 kJ/m² | 50%RH | ISO 179/1eA | ||
23 °C | 19 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 19 kJ/m² | dry | ISO 179/1eA | ||
23 °C | 25 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 25 kJ/m² | 50%RH | ISO 179/1eA | ||
Impact strength, Charpy unnotched | 90 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 90 kJ/m² | dry | ISO 179/1eU | -30°C | |
95 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 95 kJ/m² | dry | ISO 179/1eU | 23°C | ||
100 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 100 kJ/m² | 50%RH | ISO 179/1eU | -30°C | ||
110 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 110 kJ/m² | 50%RH | ISO 179/1eU | 23°C | ||
Tensile strength | 130 MPa Show Supplier Material materials with Tensile strength of 130 MPa | 50%RH | ISO 527-2/1A | 5mm/min | |
220 MPa Show Supplier Material materials with Tensile strength of 220 MPa | dry | ISO 527-2/1A | 5mm/min |
Thermal
Property | Value | Testing Standard | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature | 200 °C Show Supplier Material materials with Heat deflection temperature of 200 °C | ISO 75/2Af | 1.80 MPa | ||
Melting point | 220 °C Show Supplier Material materials with Melting point of 220 °C | ISO 11357-1/-3 | 10°C/min | ||
Flammability | Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3 |
Technological properties
Property | ||
---|---|---|
Additives | Release agent | |
Certifications | RoHS 2011/65/UE | |
Color | Black | |
Features | DPPD Free, Heat Stabilized | |
Fillers | 50% Glass Fiber | |
Processing methods | Injection Molding |