Properties
General
| Property | Value | Testing Standard |
|---|---|---|
Density | 1.28 g/cm³ Show Supplier Material materials with Density of 1.28 g/cm³ | ISO 1183 |
Mechanical
| Property | Temperature | Value | Testing Standard | Comment |
|---|---|---|---|---|
Elastic modulus | 2.5 GPa Show Supplier Material materials with Elastic modulus of 2.5 GPa | ISO 527-2/1A | 1mm/min | |
Flexural modulus | 2.4 GPa Show Supplier Material materials with Flexural modulus of 2.4 GPa | ISO 178 | 2mm/min | |
Flexural strength | 78 MPa Show Supplier Material materials with Flexural strength of 78 MPa | ISO 178 | 2mm/min | |
Impact strength, Charpy notched | 23 °C | 8.6 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 8.6 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | 23 °C | 61 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 61 kJ/m² | ISO 179/1eU | |
Yield strength | 53 MPa Show Supplier Material materials with Yield strength of 53 MPa | ISO 527-2/1A | 50mm/min |
Thermal
| Property | Value | Thickness | Testing Standard | Comment |
|---|---|---|---|---|
Melting point | 280 °C Show Supplier Material materials with Melting point of 280 °C | 9.8 mm | ISO 11357-1/-3 | 10°C/min |
Rheological Properties
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Melt mass-flow rate | 178 g/10min Show Supplier Material materials with Melt mass-flow rate of 178 g/10min | ISO 1133 | 315°C/5Kg |
Technological properties
| Property | ||
|---|---|---|
| Certifications | RoHS 2011/65/UE | |
| Color | Natural | |
| Features | Impact Modified | |
| Processing methods | Injection Molding | |