Properties
General
| Property | Value | Testing Standard |
|---|---|---|
Density | 1.93 g/cm³ Show Supplier Material materials with Density of 1.93 g/cm³ | ISO 1183 |
Mechanical
| Property | Temperature | Value | Testing Standard | Comment |
|---|---|---|---|---|
Elastic modulus | 23.1 GPa Show Supplier Material materials with Elastic modulus of 23.1 GPa | ISO 527-2/1A | 1mm/min | |
Elongation | 0.7 % Show Supplier Material materials with Elongation of 0.7 % | ISO 527-2/1A | 5mm/min | |
Flexural modulus | 23.5 GPa Show Supplier Material materials with Flexural modulus of 23.5 GPa | ISO 178 | 2mm/min | |
Flexural strength | 215 MPa Show Supplier Material materials with Flexural strength of 215 MPa | ISO 178 | 2mm/min | |
Impact strength, Charpy notched | 23 °C | 5 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 5 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | 23 °C | 13 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 13 kJ/m² | ISO 179/1eU | |
Impact strength, Izod notched | 23 °C | 5.5 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 5.5 kJ/m² | ISO 180/1A | |
Tensile strength | 144 MPa Show Supplier Material materials with Tensile strength of 144 MPa | ISO 527-2/1A | 5mm/min |
Thermal
| Property | Value | Testing Standard | Comment | ||
|---|---|---|---|---|---|
Coefficient of thermal expansion | 1.8e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.8e-05 1/K | ISO 11359-1/-2 | 23°C-55°C | ||
3.2e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 3.2e-05 1/K | ISO 11359-1/-2 | 23°C-55°C, Transverse | |||
Heat deflection temperature | 260 °C Show Supplier Material materials with Heat deflection temperature of 260 °C | ISO 75/2Af | 1.80 MPa | ||
275 °C Show Supplier Material materials with Heat deflection temperature of 275 °C | ISO 75/2Bf | 0.45 MPa | |||
Melting point | 280 °C Show Supplier Material materials with Melting point of 280 °C | ISO 11357-1/-3 | 10°C/min | ||
Flammability | Thickness tested (mm): 0.8, Class: V-0, Standard: UL 94 | ||||
Electrical
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Comparative tracking index | 150 V Show Supplier Material materials with Comparative tracking index of 150 V | IEC 60112 | Sol.A |
Rheological Properties
| Property | Value | Testing Standard | Condition | Comment |
|---|---|---|---|---|
Melt mass-flow rate | 50 g/10min Show Supplier Material materials with Melt mass-flow rate of 50 g/10min | ISO 1133 | 315°C/5Kg | |
Shrinkage | 0.2 % Show Supplier Material materials with Shrinkage of 0.2 % | ISO 294-4 | 330/140/50* | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
0.6 % Show Supplier Material materials with Shrinkage of 0.6 % | ISO 294-4 | 330/140/50* | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse |
Technological properties
| Property | ||
|---|---|---|
| Additives | Release agent | |
| Certifications | RoHS 2011/65/UE | |
| Color | Natural | |
| Features | Improved Dimensional Stability, Flame Retardant, Heat Stabilized | |
| Fillers | 65% Glass Fiber and Mineral Powder | |
| Processing methods | Injection Molding | |