Properties
General
| Property | Value | Testing Standard |
|---|---|---|
Density | 1.49 g/cm³ Show Supplier Material materials with Density of 1.49 g/cm³ | ISO 1183 |
Mechanical
| Property | Temperature | Value | Testing Standard | Comment |
|---|---|---|---|---|
Elastic modulus | 9.4 GPa Show Supplier Material materials with Elastic modulus of 9.4 GPa | ISO 527-2/1A | 1mm/min | |
Elongation | 3.6 % Show Supplier Material materials with Elongation of 3.6 % | ISO 527-2/1A | 5mm/min | |
Flexural modulus | 8.1 GPa Show Supplier Material materials with Flexural modulus of 8.1 GPa | ISO 178 | 2mm/min | |
Flexural strength | 190 MPa Show Supplier Material materials with Flexural strength of 190 MPa | ISO 178 | 2mm/min | |
Impact strength, Charpy notched | 23 °C | 16 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 16 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | 23 °C | 80 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 80 kJ/m² | ISO 179/1eU | |
Tensile strength | 124 MPa Show Supplier Material materials with Tensile strength of 124 MPa | ISO 527-2/1A | 5mm/min |
Thermal
| Property | Value | Testing Standard | Thickness | Comment | |||
|---|---|---|---|---|---|---|---|
Coefficient of thermal expansion | 2e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2e-05 1/K | ISO 11359-1/-2 | 23°C-55°C | ||||
0.00015 1/K Show Supplier Material materials with Coefficient of thermal expansion of 0.00015 1/K | ISO 11359-1/-2 | 23°C-55°C, Transverse | |||||
Glow Wire Flammability Index | 700 °C Show Supplier Material materials with Glow Wire Flammability Index of 700 °C | IEC 60695-2-12 | 2 mm | ||||
Heat deflection temperature | 204 °C Show Supplier Material materials with Heat deflection temperature of 204 °C | ISO 75/2Af | 1.80 MPa | ||||
Melting point | 225 °C Show Supplier Material materials with Melting point of 225 °C | ISO 11357-1/-3 | 10°C/min | ||||
Flammability | Thickness tested (mm): 1.5, Class: HB, Standard: UL 94 | Automotive Interior Flammability(mm/min): <30 ,method: ISO 3795 and thickness tested (mm): 3 | ||||||
Electrical
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Comparative tracking index | 550 V Show Supplier Material materials with Comparative tracking index of 550 V | IEC 60112 | Sol.A |
Surface resistivity | 1e+10 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq | IEC 60093 | 500V |
1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | IEC 60093 | 500V | |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | IEC 60093 | 500V |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | IEC 60093 | 500V |
Rheological Properties
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Shrinkage | 0.3 % Show Supplier Material materials with Shrinkage of 0.3 % | 280/80/30* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
0.9 % Show Supplier Material materials with Shrinkage of 0.9 % | 280/80/30* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse |
Technological properties
| Property | ||
|---|---|---|
| Additives | Release agent | |
| Certifications | RoHS 2011/65/UE | |
| Color | Black | |
| Features | Improved Fluiditiy, Hydrolysis Resistance, Laser Markable, Impact Modified, Heat Stabilized | |
| Fillers | 32% Glass Fiber | |
| Processing methods | Injection Molding | |