General
Property | Value | Condition | Testing Standard |
---|---|---|---|
Density | 1.4 g/cm³ Show Supplier Material materials with Density of 1.4 g/cm³ | dry | ISO 1183 |
Mechanical
Property | Temperature | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|---|
Elastic modulus | 11.5 GPa Show Supplier Material materials with Elastic modulus of 11.5 GPa | dry | ISO 527-2/1A | 1mm/min | |
Elongation | 2.2 % Show Supplier Material materials with Elongation of 2.2 % | dry | ISO 527-2/1A | 5mm/min | |
Flexural modulus | 10.3 GPa Show Supplier Material materials with Flexural modulus of 10.3 GPa | dry | ISO 178 | 2mm/min | |
Flexural strength | 260 MPa Show Supplier Material materials with Flexural strength of 260 MPa | dry | ISO 178 | 2mm/min | |
Impact strength, Charpy notched | 23 °C | 7 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 7 kJ/m² | dry | ISO 179/1eA | |
Impact strength, Charpy unnotched | 55 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 55 kJ/m² | dry | ISO 179/1eU | 23°C | |
Tensile strength | 160 MPa Show Supplier Material materials with Tensile strength of 160 MPa | dry | ISO 527-2/1A | 5mm/min |
Thermal
Rheological Properties
Property | Value | Testing Standard | Comment |
---|---|---|---|
Melt volume-flow rate | 35 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 35 cm³/10min | ISO 1133 | 275°C/5Kg |
Technological properties
Property | ||
---|---|---|
Additives | Release agent | |
Certifications | RoHS 2011/65/UE | |
Color | Black | |
Features | Heat Stabilized | |
Fillers | 35% Glass Fiber | |
Processing methods | Injection Molding |