RENYCLE S GF2501 HF0 3033 BK

Alternative and trade names
PA6-GF25 FR(40)

Want to keep this datasheet? Save it now in your required format

Description

Partially recycled PA6 flame retardant injection moulding grade, halogen and red phosphorus free. 25% glass-fibre-reinforced. Laser markable. Black colour.

This material has been developed to reduce its environmental impact compared to first-choice grades, through the recovery of post-consumer (end-of-life) components previously classified as waste. Suitable for parts requiring fire retardancy along with medium stiffness and good mechanical resistance. Tested V-0 at 0.8 mm according to UL-94.

Equivalent Materials

This material data has been provided by Radici Group.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

RADICIGROUP HIGH PERFORMANCE POLYMERS

MANUFACTURER

Additional services:

CAE Service: Customized technical support contributing to the success of innovative projects, including metal replacement applications, realized using RADILON®, RADITECK®, RADISTRONG®, RADIFLAM® and RADITER® engineering plastics. This is what RadiciGroup High Performance Polymers can offer its customers, thanks to its state-of-the-art computer-aided engineering (CAE) virtual simulation tools and the experience of its technical specialists.

Materials by this supplier

RADILON A CP300K 333 BK

RADILON AESTUS T1 RV300FC 306K BK

TORZEN Marathon G3500XHL BK20

RADILON NeXTreme RV500HHR 3800 BK

RADITER B RV300 100 NT

See all materials by this supplier

Use cases

Webinar: Metal Replacement with Engineering Polymers

Properties

General

Property	Value	Condition	Testing Standard
Density	1.38 g/cm³ Show Supplier Material materials with Density of 1.38 g/cm³	dry	ISO 1183

Mechanical

Property	Value	Condition	Testing Standard	Comment
Elastic modulus	9.4 GPa Show Supplier Material materials with Elastic modulus of 9.4 GPa	dry	ISO 527-2/1A	1mm/min
Elongation	2.9 % Show Supplier Material materials with Elongation of 2.9 %	dry	ISO 527-2/1A	5mm/min
Flexural modulus	9.1 GPa Show Supplier Material materials with Flexural modulus of 9.1 GPa	dry	ISO 178	2mm/min
Flexural strength	190 MPa Show Supplier Material materials with Flexural strength of 190 MPa	dry	ISO 178	2mm/min
Impact strength, Charpy unnotched	7 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 7 kJ/m²	dry	ISO 179/1eU	-30°C
	50 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 50 kJ/m²	dry	ISO 179/1eU	23°C
Tensile strength	120 MPa Show Supplier Material materials with Tensile strength of 120 MPa	dry	ISO 527-2/1A	5mm/min

Thermal

Property	Value	Testing Standard	Comment
Melting point	217 °C Show Supplier Material materials with Melting point of 217 °C	ISO 11357-1/-3	10°C/min
Flammability	Thickness tested (mm): 0.8, Class: V-0, Standard: UL 94

Technological properties

Property
Additives	Release agent, Flame retarding agent
Certifications	RoHS 2011/65/UE
Color	Black
Features	Laser Markable, Flame Retardant, Halogen-free, Phosphorus-free
Fillers	25% Glass Fiber
Processing methods	Injection Molding