Properties
General
| Property | Value | Condition | Testing Standard |
|---|---|---|---|
Density | 1.39 g/cm³ Show Supplier Material materials with Density of 1.39 g/cm³ | dry | ISO 1183 |
Mechanical
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Elastic modulus | 10.8 GPa Show Supplier Material materials with Elastic modulus of 10.8 GPa | dry | ISO 527-2/1A | 1mm/min | |
Elongation | 3.3 % Show Supplier Material materials with Elongation of 3.3 % | dry | ISO 527-2/1A | 5mm/min | |
Flexural modulus | 10.4 GPa Show Supplier Material materials with Flexural modulus of 10.4 GPa | dry | ISO 178 | 2mm/min | |
Flexural strength | 315 MPa Show Supplier Material materials with Flexural strength of 315 MPa | dry | ISO 178 | 2mm/min | |
Impact strength, Charpy notched | 23 °C | 14 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 14 kJ/m² | dry | ISO 179/1eA | |
Impact strength, Charpy unnotched | 86 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 86 kJ/m² | dry | ISO 179/1eU | 23°C | |
Impact strength, Izod notched | 23 °C | 14 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 14 kJ/m² | dry | ISO 180/1A | |
Tensile strength | 209 MPa Show Supplier Material materials with Tensile strength of 209 MPa | dry | ISO 527-2/1A | 5mm/min |
Thermal
| Property | Value | Testing Standard | Comment | ||
|---|---|---|---|---|---|
Melting point | 262 °C Show Supplier Material materials with Melting point of 262 °C | ISO 11357-1/-3 | 10°C/min | ||
Flammability | Thickness tested (mm): 0.8, Class: HB, Standard: UL 94 | Automotive Interior Flammability(mm/min): <100 ,method: ISO 3795 and thickness tested (mm): 2 | ||||
Technological properties
| Property | ||
|---|---|---|
| Certifications | RoHS 2011/65/UE | |
| Color | Black | |
| Fillers | 33% Glass Fiber | |
| Processing methods | Injection Molding | |