Dimension
Property | Value |
---|---|
Thickness | 300 - 420 mm Show Supplier Material materials with Thickness of 300 - 420 mm |
Width | 800 - 950 mm Show Supplier Material materials with Width of 800 - 950 mm |
Mechanical
Property | Value | Temperature | Comment |
---|---|---|---|
Hardness, Brinell | 220 [-] Show Supplier Material materials with Hardness, Brinell of 220 [-] at 23.0 °C | 23.0 °C | soft annealed |
Hardness, Rockwell C | 40 - 52 [-] Show Supplier Material materials with Hardness, Rockwell C of 40 - 52 [-] at 23.0 °C | 23.0 °C | |
Tensile strength | 1255 - 1775 MPa Show Supplier Material materials with Tensile strength of 1255 - 1775 MPa at 23.0 °C | 23.0 °C |
Thermal
Property | Value | Temperature | Comment |
---|---|---|---|
Coefficient of thermal expansion | 1.2E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.2E-5 1/K at 100.0 °C | 100.0 °C | for 20°C to the mentioned temperature |
1.23E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.23E-5 1/K at 200.0 °C | 200.0 °C | for 20°C to the mentioned temperature | |
1.27E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.27E-5 1/K at 300.0 °C | 300.0 °C | for 20°C to the mentioned temperature | |
1.31E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.31E-5 1/K at 400.0 °C | 400.0 °C | for 20°C to the mentioned temperature | |
Thermal conductivity | 44 W/(m·K) Show Supplier Material materials with Thermal conductivity of 44 W/(m·K) at 100.0 °C | 100.0 °C | |
43 W/(m·K) Show Supplier Material materials with Thermal conductivity of 43 W/(m·K) at 200.0 °C | 200.0 °C | ||
41 W/(m·K) Show Supplier Material materials with Thermal conductivity of 41 W/(m·K) at 300.0 °C | 300.0 °C | ||
39 W/(m·K) Show Supplier Material materials with Thermal conductivity of 39 W/(m·K) at 400.0 °C | 400.0 °C | ||
Chemical properties
Property | ||
---|---|---|
Carbon | 0.45 % | |
Chromium | 1.5 % | |
Iron | Balance | |
Manganese | 0.9 % | |
Nickel | 0.9 % | |
Vanadium | 1.5 % |
Technological properties
Property | ||
---|---|---|
Application areas | Special steel for press hardening, also useable for small plastic injection moulds | |
Heat Treatment | Soft annealing: 860°C (Cooling in furnace) - Hardening: 1080-1120°C and quenching in air, oil or hot bath T=500-550°C |