Formadur 2312 Plate

Alternative and trade names
DIN EN ISO 40CrMnMoS8-6, AISI P20+S, 1.2312
Want to keep this datasheet? Save it now in your required format

Description

1.2312 (40CrMnMoS8-6) is a quenched and tempered plastic mould steel with a hardness in as-delivered condition of 280 to 325 HB. Improved machinability and polishability.

Equivalent Materials

This material data has been provided by Deutsche Edelstahlwerke Specialty Steel (DEW).

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

Dimension

PropertyValue

Thickness

20 - 400 mm

Show Supplier Material materials with Thickness of 20 - 400 mm

Width

1010 mm

Show Supplier Material materials with Width of 1010 mm

Mechanical

PropertyValueComment

Hardness, Brinell

280 - 325 [-]

Show Supplier Material materials with Hardness, Brinell of 280 - 325 [-]

as-delivered condition

Hardness, Rockwell C

28 - 51 [-]

Show Supplier Material materials with Hardness, Rockwell C of 28 - 51 [-]

Tensile strength

950 - 1095 MPa

Show Supplier Material materials with Tensile strength of 950 - 1095 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

100 °C

1.23e-05 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 1.23e-05 1/K

for 20°C to the mentioned temperature | Quenched and Tempered

200 °C

1.3e-05 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 1.3e-05 1/K

for 20°C to the mentioned temperature | Quenched and Tempered

300 °C

1.37e-05 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 1.37e-05 1/K

for 20°C to the mentioned temperature | Quenched and Tempered

Thermal conductivity

100 °C

39.8 W/(m·K)

Show Supplier Material materials with Thermal conductivity of 39.8 W/(m·K)

150 °C

40.4 W/(m·K)

Show Supplier Material materials with Thermal conductivity of 40.4 W/(m·K)

200 °C

40.4 W/(m·K)

Show Supplier Material materials with Thermal conductivity of 40.4 W/(m·K)

250 °C

39.9 W/(m·K)

Show Supplier Material materials with Thermal conductivity of 39.9 W/(m·K)

300 °C

39 W/(m·K)

Show Supplier Material materials with Thermal conductivity of 39 W/(m·K)

Chemical properties

PropertyValue

Carbon

0.4 %

Show Supplier Material materials with Carbon of 0.4 %

Chromium

1.9 %

Show Supplier Material materials with Chromium of 1.9 %

Iron

Balance

Manganese

1.5 %

Show Supplier Material materials with Manganese of 1.5 %

Molybdenum

0.2 %

Show Supplier Material materials with Molybdenum of 0.2 %

Silicon

0.3 %

Show Supplier Material materials with Silicon of 0.3 %

Sulfur

0.05 %

Show Supplier Material materials with Sulfur of 0.05 %

Technological properties

Property
Application areas

Mould frames for plastic and die casting moulds, press brake dies, plastic moulds without special requirements on surface quality.

Heat Treatment

Soft annealing: 710-740°C (Cooling in furnace) - Stress relief annealing cooling in furnace (annealed): approx 600°C - Stress relief annealing cooling in furnace (quenched and tempered): approx 30-50°C under tempering temperature - Hardening: 840-870°C and quenching in oil or salt bath T=180-220°C