Properties
General
| Property | Value |
|---|---|
Density | 7.4 g/cm³ Show Supplier Material materials with Density of 7.4 g/cm³ |
Grain structure | Titanium carbide + austenite |
Mechanical
| Property | Value |
|---|---|
Compressive strength | 1500 MPa Show Supplier Material materials with Compressive strength of 1500 MPa |
Elastic modulus | 277 GPa Show Supplier Material materials with Elastic modulus of 277 GPa |
Flexural strength | 1300 MPa Show Supplier Material materials with Flexural strength of 1300 MPa |
Hardness, Rockwell C | 54 [-] Show Supplier Material materials with Hardness, Rockwell C of 54 [-] |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 100 °C | 9e-06 1/K Show Supplier Material materials with Coefficient of thermal expansion of 9e-06 1/K | for 20°C to the mentioned temperature |
200 °C | 1e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1e-05 1/K | for 20°C to the mentioned temperature | |
300 °C | 1.05e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.05e-05 1/K | for 20°C to the mentioned temperature | |
400 °C | 1.08e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.08e-05 1/K | for 20°C to the mentioned temperature | |
500 °C | 1.11e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.11e-05 1/K | for 20°C to the mentioned temperature | |
600 °C | 1.15e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.15e-05 1/K | for 20°C to the mentioned temperature | |
Thermal conductivity | 12.4 W/(m·K) Show Supplier Material materials with Thermal conductivity of 12.4 W/(m·K) |
Electrical
| Property | Value |
|---|---|
Electrical resistivity | 1.53e-06 Ω·m Show Supplier Material materials with Electrical resistivity of 1.53e-06 Ω·m |
Magnetic
| Property | Value | Comment |
|---|---|---|
Relative magnetic permeability | 1 [-] Show Supplier Material materials with Relative magnetic permeability of 1 [-] | max. |
Chemical properties
Technological properties
| Property | ||
|---|---|---|
| Application areas | This austenitic grade is used for applications requiring complete non-magnetisability, a high wear resistance and maximum corrosion resistance. | |
| Corrosion properties | Besides having a high wear resistance, this alloy is extremely resistant to corrosion and scaling, as well as highly tempering-resistant. This corrosion resistance is at its best with finely ground or polished surfaces. | |
| General machinability | In as-delivered condition, this material can be machined by conventional methods. | |
| Heat Treatment | Solution Anealing: 1200°C, 2 hr in vacuum (Cooling 4 bar N2) Hardness: 52 HRC - Age-Hardening 800°C, 6 hr in Vacuum, Hardness: 54 HRC | |