General
Property | Value |
---|---|
Density | 7.7 g/cm³ Show Supplier Material materials with Density of 7.7 g/cm³ |
Dimension
Property | Value | Comment |
---|---|---|
Diameter | 160 mm Show Supplier Material materials with Diameter of 160 mm | max. |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Charpy impact energy, V-notch | 25 J Show Supplier Material materials with Charpy impact energy, V-notch of 25 J | ||
Elastic modulus | 20 °C | 215 GPa Show Supplier Material materials with Elastic modulus of 215 GPa | |
100 °C | 212 GPa Show Supplier Material materials with Elastic modulus of 212 GPa | ||
200 °C | 205 GPa Show Supplier Material materials with Elastic modulus of 205 GPa | ||
300 °C | 200 GPa Show Supplier Material materials with Elastic modulus of 200 GPa | ||
400 °C | 190 GPa Show Supplier Material materials with Elastic modulus of 190 GPa | ||
Elongation | 13 % Show Supplier Material materials with Elongation of 13 % | A5 | |
Hardness, Brinell | 230 [-] Show Supplier Material materials with Hardness, Brinell of 230 [-] | annealed | |
Tensile strength | 700 - 850 MPa Show Supplier Material materials with Tensile strength of 700 - 850 MPa | ||
Yield strength | 20 °C | 500 MPa Show Supplier Material materials with Yield strength of 500 MPa | RP02 |
100 °C | 460 MPa Show Supplier Material materials with Yield strength of 460 MPa | RP02 | |
150 °C | 445 MPa Show Supplier Material materials with Yield strength of 445 MPa | RP02 | |
200 °C | 430 MPa Show Supplier Material materials with Yield strength of 430 MPa | RP02 | |
250 °C | 415 MPa Show Supplier Material materials with Yield strength of 415 MPa | RP02 | |
300 °C | 395 MPa Show Supplier Material materials with Yield strength of 395 MPa | RP02 | |
350 °C | 365 MPa Show Supplier Material materials with Yield strength of 365 MPa | RP02 | |
400 °C | 330 MPa Show Supplier Material materials with Yield strength of 330 MPa | RP02 |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 100 °C | 1.05e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.05e-05 1/K | for 20°C to the mentioned temperature |
200 °C | 1.1e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.1e-05 1/K | for 20°C to the mentioned temperature | |
300 °C | 1.15e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.15e-05 1/K | for 20°C to the mentioned temperature | |
400 °C | 1.2e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.2e-05 1/K | for 20°C to the mentioned temperature | |
Specific heat capacity | 460 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 460 J/(kg·K) | ||
Thermal conductivity | 30 W/(m·K) Show Supplier Material materials with Thermal conductivity of 30 W/(m·K) |
Electrical
Property | Value |
---|---|
Electrical resistivity | 6e-07 Ω·m Show Supplier Material materials with Electrical resistivity of 6e-07 Ω·m |
Chemical properties
Property | Value |
---|---|
Carbon | 0.16 - 0.25 % Show Supplier Material materials with Carbon of 0.16 - 0.25 % |
Chromium | 12 - 14 % Show Supplier Material materials with Chromium of 12 - 14 % |
Iron | Balance |
Manganese | 1 % Show Supplier Material materials with Manganese of 1 % |
Molybdenum | 0.5 % Show Supplier Material materials with Molybdenum of 0.5 % |
Nickel | 0.5 % Show Supplier Material materials with Nickel of 0.5 % |
Phosphorus | 0.04 % Show Supplier Material materials with Phosphorus of 0.04 % |
Silicon | 1 % Show Supplier Material materials with Silicon of 1 % |
Sulfur | 0.01 - 0.03 % Show Supplier Material materials with Sulfur of 0.01 - 0.03 % |
Technological properties
Property | ||
---|---|---|
Application areas | Automotive industry, Decorative Applications, Hydraulic Equipment, Petrochemical industry, Food and Beverage industry, Mechanical engineering, Cutlery, Blades | |
Corrosion properties | Average - Good corrosion resistance in moderately corrosive environments that are free of chlorides, such as soaps, detergents and organic acids. Good resistance in oxidising atmospheres up to temperatures of about 600 °C. 1.4021 is not resistant to intergranular corrosion in the asdelivered or as-welded conditions. PRE = 12.0 – 14.0 | |
General machinability | Good - The machinability of this grade of stainless steel is directly related to its hardness. 1.4021 machines similar to carbon steels of the same hardness. Although it must be realised that the machining parameters will vary depending on the structure/hardness of the steel. | |
Heat Treatment | Soft annealing: 745-825°C (Cooling in furnace, air) - Hardening: 950-1050°C and quenching in air, polymer, oil - Tempering: 650-750°C | |
Hot forming | It is formable at 800-1100°C | |
Processing history | Quenched and tempered, QT 700 | |
Welding | Good - Preheating of the work piece to a temperature within the range 100 °C – 300 °C is required as well as a post weld tempering treatment when welding is performed using a matching filler material. Generally, Novonit® 4551 is recommended when a filler material is required. Tempering at 650 °C after welding is recommended to restore some of the ductility in the weld zone. When using an inert or protective shielding gas during welding, care must be taken to avoid use of any hydrogen or nitrogen containing gases since contamination of the weld with nitrogen or hydrogen will adversely affect the mechanical properties. After welding the work piece must be cooled to below the martensite start (MS), temperature of approximately 120 °C before being tempered. |