Properties
General
| Property | Value |
|---|---|
Density | 7.6 g/cm³ Show Supplier Material materials with Density of 7.6 g/cm³ |
Dimension
| Property | Value | Comment |
|---|---|---|
Diameter | 250 mm Show Supplier Material materials with Diameter of 250 mm | max. |
Mechanical
| Property | Value | Comment |
|---|---|---|
Charpy impact energy, V-notch | 30 - 35 J Show Supplier Material materials with Charpy impact energy, V-notch of 30 - 35 J | |
Elastic modulus | 210 GPa Show Supplier Material materials with Elastic modulus of 210 GPa | |
Elongation | 10 - 13 % Show Supplier Material materials with Elongation of 10 - 13 % | A5 |
Hardness, Brinell | 248 [-] Show Supplier Material materials with Hardness, Brinell of 248 [-] | annealed |
Tensile strength | 800 - 1100 MPa Show Supplier Material materials with Tensile strength of 800 - 1100 MPa | |
Yield strength | 600 - 680 MPa Show Supplier Material materials with Yield strength of 600 - 680 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 100 °C | 1.11e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.11e-05 1/K | for 20°C to the mentioned temperature |
200 °C | 1.21e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.21e-05 1/K | for 20°C to the mentioned temperature | |
300 °C | 1.29e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.29e-05 1/K | for 20°C to the mentioned temperature | |
400 °C | 1.35e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.35e-05 1/K | for 20°C to the mentioned temperature | |
Specific heat capacity | 420 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 420 J/(kg·K) | ||
Thermal conductivity | 42.6 W/(m·K) Show Supplier Material materials with Thermal conductivity of 42.6 W/(m·K) |
Electrical
| Property | Value |
|---|---|
Electrical resistivity | 1.9e-07 Ω·m Show Supplier Material materials with Electrical resistivity of 1.9e-07 Ω·m |
Chemical properties
| Property | Value |
|---|---|
Aluminium | 0.8 - 1.2 % Show Supplier Material materials with Aluminium of 0.8 - 1.2 % |
Carbon | 0.3 - 0.37 % Show Supplier Material materials with Carbon of 0.3 - 0.37 % |
Chromium | 1.5 - 1.8 % Show Supplier Material materials with Chromium of 1.5 - 1.8 % |
Iron | Balance |
Manganese | 0.4 - 0.7 % Show Supplier Material materials with Manganese of 0.4 - 0.7 % |
Molybdenum | 0.15 - 0.25 % Show Supplier Material materials with Molybdenum of 0.15 - 0.25 % |
Nickel | 0.85 - 1.15 % Show Supplier Material materials with Nickel of 0.85 - 1.15 % |
Phosphorus | 0.025 % Show Supplier Material materials with Phosphorus of 0.025 % |
Silicon | 0.4 % Show Supplier Material materials with Silicon of 0.4 % |
Sulfur | 0.035 % Show Supplier Material materials with Sulfur of 0.035 % |
Technological properties
| Property | ||
|---|---|---|
| Application areas | It is used in Automotive and Mechanical engineering for heat-treated components which have been subjected to very high wear stresses, such as cam plates, eccentrics or pinion shafts. | |
| Heat Treatment | Soft annealing: 650-700°C (Slow furnace cooling down), Quenching: 870-930°C (Oil, Water, Polymer), Tempering: 580-700°C (Air), Nitriding: 480-570°C | |
| Hot forming | It is formable at 850-1050°C and should then cooled slowly. | |
| Processing history | Quenched and Tempered | |
| Welding | It is difficult to weld and should will not used be in welded constructions. | |