General
Property | Value |
---|---|
Density | 7.8 g/cm³ Show Supplier Material materials with Density of 7.8 g/cm³ |
Dimension
Property | Value | Comment |
---|---|---|
Diameter | 100 mm Show Supplier Material materials with Diameter of 100 mm | max. |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 20 °C | 200 GPa Show Supplier Material materials with Elastic modulus of 200 GPa | |
100 °C | 195 GPa Show Supplier Material materials with Elastic modulus of 195 GPa | ||
200 °C | 185 GPa Show Supplier Material materials with Elastic modulus of 185 GPa | ||
300 °C | 175 GPa Show Supplier Material materials with Elastic modulus of 175 GPa | ||
400 °C | 170 GPa Show Supplier Material materials with Elastic modulus of 170 GPa | ||
Elongation | 10 % Show Supplier Material materials with Elongation of 10 % | A5 | |
Hardness, Brinell | 360 [-] Show Supplier Material materials with Hardness, Brinell of 360 [-] | annealed | |
Tensile strength | 1070 - 1270 MPa Show Supplier Material materials with Tensile strength of 1070 - 1270 MPa | ||
Yield strength | 23 °C | 1000 MPa Show Supplier Material materials with Yield strength of 1000 MPa | RP02 |
100 °C | 880 MPa Show Supplier Material materials with Yield strength of 880 MPa | RP02 | |
150 °C | 830 MPa Show Supplier Material materials with Yield strength of 830 MPa | RP02 | |
200 °C | 800 MPa Show Supplier Material materials with Yield strength of 800 MPa | RP02 | |
250 °C | 770 MPa Show Supplier Material materials with Yield strength of 770 MPa | RP02 | |
300 °C | 750 MPa Show Supplier Material materials with Yield strength of 750 MPa | RP02 |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 100 °C | 1.09e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.09e-05 1/K | for 20°C to the mentioned temperature |
200 °C | 1.11e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.11e-05 1/K | for 20°C to the mentioned temperature | |
Specific heat capacity | 500 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 500 J/(kg·K) | ||
Thermal conductivity | 16 W/(m·K) Show Supplier Material materials with Thermal conductivity of 16 W/(m·K) |
Electrical
Property | Value |
---|---|
Electrical resistivity | 7.1e-07 Ω·m Show Supplier Material materials with Electrical resistivity of 7.1e-07 Ω·m |
Chemical properties
Property | Value |
---|---|
Carbon | 0.07 % Show Supplier Material materials with Carbon of 0.07 % |
Chromium | 15 - 17 % Show Supplier Material materials with Chromium of 15 - 17 % |
Copper | 3 - 5 % Show Supplier Material materials with Copper of 3 - 5 % |
Iron | Balance |
Manganese | 1 % Show Supplier Material materials with Manganese of 1 % |
Molybdenum | 0.6 % Show Supplier Material materials with Molybdenum of 0.6 % |
Nickel | 3 - 5 % Show Supplier Material materials with Nickel of 3 - 5 % |
Other | 0.15 - 0.45 % Show Supplier Material materials with Other of 0.15 - 0.45 % |
Phosphorus | 0.04 % Show Supplier Material materials with Phosphorus of 0.04 % |
Silicon | 0.7 % Show Supplier Material materials with Silicon of 0.7 % |
Sulfur | 0.03 % Show Supplier Material materials with Sulfur of 0.03 % |
Technological properties
Property | ||
---|---|---|
Application areas | Aerospace, Plant engineering and construction, Chemical industry, Wood industry, Mechanical engineering, Oil industry, Paper industry, Sports and leisure industry, Ship building | |
Corrosion properties | The good combination of high corrosion resistance and good mechanical properties makes Acidur 4542 suitable for use in marine environments. In standing seawater, however, Acidur 4542 is susceptible to crevice corrosion. If application in standing seawater cannot be excluded, additional protection (e.g. painting) must be applied. | |
General machinability | Acidur 4542 can be machined in both the solution annealed and hardened condition. The machinability of Acidur 4542 depends on the hardness | |
Heat Treatment | Hardening:1030-1055°C in oil, air - Percipitation hardening: 4 hr 550°C in air | |
Hot forming | It is formable at 900-1150°C | |
Processing history | Percipitation hardened P1070 | |
Welding | To weld Acidur 4542, the condition of the base material must be taken into account. The copper is present in the material in a stable form and therefore does not promote hot cracking. In addition to setting optimum welding conditions, care must be taken to avoid undercuts or other welding defects that lead to the formation of a notch. After welding, the material must be solution annealed again within a very short time with subsequent ageing to prevent stress cracking. |