CR1 1019GH60

Alternative and trade names
CR1 1019GH60
Want to keep this datasheet? Save it now in your required format

Description

For profile extrusion application.

This material data has been provided by Indochine Bio Plastiques (ICBP) Sdn. Bhd..

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValue

Bio-based content

100 %

Show Supplier Material materials with Bio-based content of 100 %

Density

23.0 °C

1.05 g/cm³

Show Supplier Material materials with Density of 1.05 g/cm³

Mechanical

PropertyTemperatureValue

Elongation

23.0 °C

29 %

Show Supplier Material materials with Elongation of 29 %

Flexural modulus

23.0 °C

0.44 GPa

Show Supplier Material materials with Flexural modulus of 0.44 GPa

Flexural strength

23.0 °C

8 MPa

Show Supplier Material materials with Flexural strength of 8 MPa

Hardness, Shore D

23.0 °C

62 [-]

Show Supplier Material materials with Hardness, Shore D of 62 [-]

Impact strength, Izod unnotched, ASTM

23.0 °C

30 J/m

Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 30 J/m

Tensile strength

23.0 °C

18 MPa

Show Supplier Material materials with Tensile strength of 18 MPa

Thermal

PropertyValue

Max service temperature

185 °C

Show Supplier Material materials with Max service temperature of 185 °C

Melting point

132 °C

Show Supplier Material materials with Melting point of 132 °C

Rheological Properties

PropertyValueComment

Melt mass-flow rate

18 g/10min

Show Supplier Material materials with Melt mass-flow rate of 18 g/10min

175°C/5 kg

Technological properties

Property
Application areas

Toy, tube, profile extrusion

Certifications

Food Contact: Halal

Processing methods

1. Clean extruder with general purpose polyethylene or polypropylene. 2. Vacuum out hopper system to avoid contamination and make sure that the humidity of the air is below 40°C at dew point. 3. Introduce ICBP Bio Resin in to the extruder at the operating conditions used in the first step. 4. Once ICBP Bio Resin has been purged, reduce barrel temperatures to desired set points. 5. At shutdown, purge machine with PE or PP.