General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 20.0 °C | 0.91 g/cm³ Show Material materials with Density of 0.91 g/cm³ | |
Film yield | 20.0 °C | 27.5 - 54.9 m²/kg Show Material materials with Film yield of 27.5 - 54.9 m²/kg | |
Shrinkage | 120.0 °C | 4 % Show Material materials with Shrinkage of 4 % | GOST 18616, ISO 11501, ASTM D1204 (Thermal shrinkage at 120˚C, 5 min) |
Shrinkage, transverse | 120.0 °C | 2 % Show Material materials with Shrinkage, transverse of 2 % | GOST 18616, ISO 11501, ASTM D1204 (Thermal shrinkage at 120˚C, 5 min) |
Surface density | 20.0 °C | 1.82E-3 - 3.64E-3 g/cm² Show Material materials with Surface density of 1.82E-3 - 3.64E-3 g/cm² |
Dimension
| Property | Value |
|---|---|
Thickness | 0.02 - 0.04 mm Show Material materials with Thickness of 0.02 - 0.04 mm |
Dimensions | Available thicknesses: 20, 25, 30, 35, 40µm. |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongation | 20.0 °C | 200 % Show Material materials with Elongation of 200 % | GOST 14236, ISO 527, ASTM D882 |
Elongation, transverse | 20.0 °C | 70 % Show Material materials with Elongation, transverse of 70 % | GOST 14236, ISO 527, ASTM D883 |
Tensile strength | 20.0 °C | 140 MPa Show Material materials with Tensile strength of 140 MPa | GOST 14236, ISO 527, ASTM D883 |
Tensile strength, transverse | 20.0 °C | 250 MPa Show Material materials with Tensile strength, transverse of 250 MPa | GOST 14236, ISO 527, ASTM D883 |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Rotogravure and flexographic solvent based one or both side printing; for both side lamination with solvent based or solventless polyurethane adhesives; lamination with films, paper and cardboard, as well as in the center of the triplex in flexible packaging; for the production of labels with both side printed design. | |
| Friction | Kinetic coefficient of friction µ= 0.2-0.4 (GOST 27492, ISO 8295, ASTM D 1894). | |
| Other | PMP.M BOPP Films comprise: An aluminum layer, a treated modified copolymer layer for aluminum adhesion, a transparent oriented polypropylene core layer, a treated non-heat-sealable skin layer with standard coefficient of friction. | |
| Processing history | Treatment level: 36-38 mN/m (ISO 8296, ASTM D 2578). | |