General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.32 g/cm³ Show Material materials with Density of 1.32 g/cm³ | ASTM D 792 |
Water absorption | 23.0 °C | 0.07 % Show Material materials with Water absorption of 0.07 % | ISO 62 | 23°C, 50% RH |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.5 GPa Show Material materials with Elastic modulus of 2.5 GPa | ASTM D 638 | 5 mm/min |
Elongation | 23.0 °C | 2 % Show Material materials with Elongation of 2 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 2 % Show Material materials with Elongation at yield of 2 % | ASTM D 638 | Type I, 50 mm/min |
Flexural modulus | 23.0 °C | 2.29 GPa Show Material materials with Flexural modulus of 2.29 GPa | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 81 MPa Show Material materials with Flexural yield strength of 81 MPa | ISO 178 | 2 mm/min |
Impact strength, Charpy notched | 23.0 °C | 7 kJ/m² Show Material materials with Impact strength, Charpy notched of 7 kJ/m² | ISO 179/1eA |
Impact strength, Izod notched | 23.0 °C | 2 kJ/m² Show Material materials with Impact strength, Izod notched of 2 kJ/m² | ISO 180/1A |
Impact strength, Izod notched, ASTM | 23.0 °C | 28 J/m Show Material materials with Impact strength, Izod notched, ASTM of 28 J/m | ASTM D 256 |
Impact strength, Izod unnotched | 23.0 °C | 35 kJ/m² Show Material materials with Impact strength, Izod unnotched of 35 kJ/m² | ISO 180/1U |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 890 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 890 J/m | ASTM D 4812 |
Tensile strength | 23.0 °C | 50 MPa Show Material materials with Tensile strength of 50 MPa | ASTM D 638 | Type I, 50 mm/min |
Yield strength | 23.0 °C | 50 MPa Show Material materials with Yield strength of 50 MPa | ASTM D 638 | Type I, 50 mm/min |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 8.5E-5 1/K Show Material materials with Coefficient of thermal expansion of 8.5E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 8.5E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 8.5E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Heat deflection temperature, 0.45 MPa | 113 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 113 °C | ISO 75/Bf | 0.45 MPa | |
Vicat softening temperature | 177 °C Show Material materials with Vicat softening temperature of 177 °C | ISO 306 | Rate B/120 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 127 g/10min Show Material materials with Melt mass-flow rate of 127 g/10min | ASTM D 1238 | 250°C/1.2 kgf | |
Melt volume-flow rate | 231 cm³/10min Show Material materials with Melt volume-flow rate of 231 cm³/10min | ISO 1133 | 250°C/2.16 kg | |
Shrinkage | 23.0 °C | 1.5 - 1.8 % Show Material materials with Shrinkage of 1.5 - 1.8 % | SABIC method | 3.2 mm |
Shrinkage, transverse | 23.0 °C | 1.6 - 2 % Show Material materials with Shrinkage, transverse of 1.6 - 2 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Circuit Protection,Heavy Vehicles,Pharmaceutical Manufacturing,Water Treatment/Filtration | |
Processing methods | Drying Temperature: 110-120°C, Drying Time: 4-6hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 245-260°C, Barrel - Zone 1 Temperature: 200-230°C, Barrel - Zone 2 Temperature: 240-255°C, Barrel - Zone 3 Temperature: 240-275°C, Barrel - Zone 4 Temperature: 240-275°C, Adapter Temperature: 240-275°C, Die Temperature: 240-275°C |