General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.31 g/cm³ Show Material materials with Density of 1.31 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.08 % Show Material materials with Water absorption of 0.08 % | ISO 62 | 23°C, 50% RH |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 2.4 GPa Show Material materials with Elastic modulus of 2.4 GPa | ISO 527 | 1 mm/min | ||
Elongation | 23.0 °C | 30 % Show Material materials with Elongation of 30 % | ISO 527 | 50 mm/min | ||
Flexural modulus | 23.0 °C | 2.3 GPa Show Material materials with Flexural modulus of 2.3 GPa | ISO 178 | 2 mm/min | ||
Flexural yield strength | 23.0 °C | 75 MPa Show Material materials with Flexural yield strength of 75 MPa | ISO 178 | 2 mm/min | ||
Hardness, Ball Indentation | 23.0 °C | 83 MPa Show Material materials with Hardness, Ball Indentation of 83 MPa | ISO 2039-1 | ||
Impact strength, Charpy notched | -30.0 °C | 3 kJ/m² Show Material materials with Impact strength, Charpy notched of 3 kJ/m² | ISO 179/1eA | ||
23.0 °C | 4 kJ/m² Show Material materials with Impact strength, Charpy notched of 4 kJ/m² | ISO 179/1eA | |||
Impact strength, Izod notched | -30.0 °C | 3 kJ/m² Show Material materials with Impact strength, Izod notched of 3 kJ/m² | ISO 180/1A | ||
23.0 °C | 3 kJ/m² Show Material materials with Impact strength, Izod notched of 3 kJ/m² | ISO 180/1A | |||
Yield strength | 23.0 °C | 50 MPa Show Material materials with Yield strength of 50 MPa | ISO 527 | 50 mm/min | ||
Impact strength, Charpy unnotched | No Break @ 23,-30°C | ISO 179/1eU | ||||
Impact strength, Izod unnotched | No Break @ 23,-30°C | ISO 180/1U |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.3E-4 1/K Show Material materials with Coefficient of thermal expansion of 1.3E-4 1/K | ISO 11359-2 | -23°C to 80°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 1.3E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.3E-4 1/K | ISO 11359-2 | 23°C to 80°C |
Heat deflection temperature, 0.45 MPa | 158 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 158 °C | ISO 75/Be | 0.45 MPa | |
Vicat softening temperature | 175 °C Show Material materials with Vicat softening temperature of 175 °C | ISO 306 | Rate B/120 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 600 V Show Material materials with Comparative tracking index of 600 V | IEC 60112 |
Dielectric constant | 23.0 °C | 3.3 [-] Show Material materials with Dielectric constant of 3.3 [-] | IEC 60250 | at 50/60 Hz |
Dielectric strength | 23.0 °C | 18 kV/mm Show Material materials with Dielectric strength of 18 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
Dissipation factor | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor of 0.02 [-] | IEC 60250 | at 1 MHz |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt volume-flow rate | 105 cm³/10min Show Material materials with Melt volume-flow rate of 105 cm³/10min | ISO 1133 | 250°C/2.16 kg | |
Shrinkage | 23.0 °C | 1.1 - 1.8 % Show Material materials with Shrinkage of 1.1 - 1.8 % | SABIC method |
Shrinkage, transverse | 23.0 °C | 0.9 - 1.8 % Show Material materials with Shrinkage, transverse of 0.9 - 1.8 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Water Treatment/Filtration | |
Processing methods | Drying Temperature: 110-120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-270°C, Nozzle Temperature: 240-260°C, Front - Zone 3 Temperature: 245-265°C, Middle - Zone 2 Temperature: 240-255°C, Rear - Zone 1 Temperature: 230-245°C, Hopper Temperature: 40-60°C, Mold Temperature: 40-100°C |