Properties
General
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 1.96 GPa Show Material materials with Elastic modulus of 1.96 GPa | ASTM D 638 | 5 mm/min |
Elongation | 23.0 °C | 50 % Show Material materials with Elongation of 50 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 5 % Show Material materials with Elongation at yield of 5 % | ASTM D 638 | Type I, 50 mm/min |
Flexural modulus | 23.0 °C | 1.83 GPa Show Material materials with Flexural modulus of 1.83 GPa | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 69 MPa Show Material materials with Flexural yield strength of 69 MPa | ISO 178 | 2 mm/min |
Impact strength, Charpy notched | 23.0 °C | 51 kJ/m² Show Material materials with Impact strength, Charpy notched of 51 kJ/m² | ISO 179/1eA |
Impact strength, Izod notched | -30.0 °C | 17 kJ/m² Show Material materials with Impact strength, Izod notched of 17 kJ/m² | ISO 180/1A |
23.0 °C | 51 kJ/m² Show Material materials with Impact strength, Izod notched of 51 kJ/m² | ISO 180/1A | |
Impact strength, Izod notched, ASTM | -40.0 °C | 427 J/m Show Material materials with Impact strength, Izod notched, ASTM of 427 J/m | ASTM D 256 |
-20.0 °C | 694 J/m Show Material materials with Impact strength, Izod notched, ASTM of 694 J/m | ASTM D 256 | |
23.0 °C | 747 J/m Show Material materials with Impact strength, Izod notched, ASTM of 747 J/m | ASTM D 256 | |
Tensile strength | 23.0 °C | 36 MPa Show Material materials with Tensile strength of 36 MPa | ASTM D 638 | Type I, 50 mm/min |
Yield strength | 23.0 °C | 46 MPa Show Material materials with Yield strength of 46 MPa | ASTM D 638 | Type I, 50 mm/min |
Thermal
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 9.5E-5 1/K Show Material materials with Coefficient of thermal expansion of 9.5E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 9.8E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 9.8E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Heat deflection temperature, 1.80 MPa | 68 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 68 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |||
Relative temperature index, electrical | 75 °C Show Material materials with Relative temperature index, electrical of 75 °C | UL 746B | |||
Relative temperature index, mechanical impact | 75 °C Show Material materials with Relative temperature index, mechanical impact of 75 °C | UL 746B | |||
Relative temperature index, mechanical strength | 75 °C Show Material materials with Relative temperature index, mechanical strength of 75 °C | UL 746B | |||
Vicat softening temperature | 115 °C Show Material materials with Vicat softening temperature of 115 °C | ASTM D 1525 | Rate B/50 | |||
Flammability | UL Recognized, 94-5VA Flame Class Rating | 2.99mm | UL 94 | ||||
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Comparative tracking index | 23.0 °C | 0 V Show Material materials with Comparative tracking index of 0 V | UL 746A |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt mass-flow rate | 19 g/10min Show Material materials with Melt mass-flow rate of 19 g/10min | ASTM D 1238 | 266°C/5.0 kg | |
Melt volume-flow rate | 17 cm³/10min Show Material materials with Melt volume-flow rate of 17 cm³/10min | ISO 1133 | 265°C/5.0 kg | |
Shrinkage | 23.0 °C | 0.8 - 1 % Show Material materials with Shrinkage of 0.8 - 1 % | SABIC method | 3.2 mm |
Shrinkage, transverse | 23.0 °C | 0.8 - 1 % Show Material materials with Shrinkage, transverse of 0.8 - 1 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | ATM/Ticket Machine,Audio,Cooking Range,Data Transfer,Displays,Document Handling,Electronic Components,Enclosures,Energy Management,Fluid Delivery,Heavy Vehicles,Lab Ware and Clinical Diagnostics,Medical Device,Medical Facility Infrastructure,Monitoring and Imaging,Non-LED Lighting,Personal Computing,Pharmaceutical Packaging & Drug Delivery,Respiratory,Small Appliance,Surgical Devices,Wearables,Wireless Communications | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 12hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-265°C, Nozzle Temperature: 245-260°C, Front - Zone 3 Temperature: 250-265°C, Middle - Zone 2 Temperature: 245-260°C, Rear - Zone 1 Temperature: 240-255°C, Mold Temperature: 50-75°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 50-100rpm, Shot to Cylinder Size: 40-80%, Vent Depth: 0.025-0.038mm | |