VALOX™ Resin 430

Want to keep this datasheet? Save it now in your required format

Description

33 % glass reinforced, impact modified. Connectors, etc.

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.52 g/cm³

Show Material materials with Density of 1.52 g/cm³

ASTM D 792

Water absorption

23.0 °C

0.05 %

Show Material materials with Water absorption of 0.05 %

ASTM D 570 | 24 Hours

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

8.66 GPa

Show Material materials with Elastic modulus of 8.66 GPa

ASTM D 638 | 5 mm/min

Elongation

23.0 °C

3.1 %

Show Material materials with Elongation of 3.1 %

ASTM D 638 | Type I, 5 mm/min

Flexural modulus

23.0 °C

7.81 GPa

Show Material materials with Flexural modulus of 7.81 GPa

ASTM D 790 | 1.3 mm/min, 50 mm span

Flexural strength

23.0 °C

174 MPa

Show Material materials with Flexural strength of 174 MPa

ASTM D 790 | 1.3 mm/min, 50 mm span

Hardness, Rockwell R

23.0 °C

125 [-]

Show Material materials with Hardness, Rockwell R of 125 [-]

ASTM D 785

Impact strength, Izod notched, ASTM

23.0 °C

128 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 128 J/m

ASTM D 256

Impact strength, Izod unnotched, ASTM

23.0 °C

857 J/m

Show Material materials with Impact strength, Izod unnotched, ASTM of 857 J/m

ASTM D 4812

Tensile strength

23.0 °C

106 MPa

Show Material materials with Tensile strength of 106 MPa

ASTM D 638 | Type I, 5 mm/min

Thermal

PropertyValueComment

Heat deflection temperature, 1.80 MPa

208 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 208 °C

ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed

Relative temperature index, electrical

130 °C

Show Material materials with Relative temperature index, electrical of 130 °C

UL 746B

Relative temperature index, mechanical impact

130 °C

Show Material materials with Relative temperature index, mechanical impact of 130 °C

UL 746B

Relative temperature index, mechanical strength

140 °C

Show Material materials with Relative temperature index, mechanical strength of 140 °C

UL 746B

Flammability

UL Recognized, 94HB Flame Class Rating | 1.47mm | UL 94

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

1 V

Show Material materials with Comparative tracking index of 1 V

UL 746A

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

11.7 g/10min

Show Material materials with Melt mass-flow rate of 11.7 g/10min

ASTM D 1238 | 250°C/2.16 kg

Shrinkage

23.0 °C

0.5 - 0.8 %

Show Material materials with Shrinkage of 0.5 - 0.8 %

SABIC method | 3.2-4.6 mm

Shrinkage, transverse

23.0 °C

0.6 - 0.9 %

Show Material materials with Shrinkage, transverse of 0.6 - 0.9 %

SABIC method | 3.2-4.6 mm

Technological properties

Property
Application areas

Auto Aftermarket,Circuit Protection,Data Management,Data Transfer,Electronic Components,Enclosure/Housing/Cover,Enclosures,Energy Management,Food Processor,Gas/Electric Oven,Medical Device,Power Manangement,Recreational Vehicle,Water Treatment/Filtration,Wireless Communications,Wiring Devices,Wire & cable

Fillers

33% Glass Fiber

Processing methods

Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 12hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-265°C, Nozzle Temperature: 245-260°C, Front - Zone 3 Temperature: 250-265°C, Middle - Zone 2 Temperature: 245-260°C, Rear - Zone 1 Temperature: 240-255°C, Mold Temperature: 65-90°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 50-80rpm, Shot to Cylinder Size: 40-80%, Vent Depth: 0.025-0.038mm