General
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 9 GPa Show Material materials with Elastic modulus of 9 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 2 % Show Material materials with Elongation of 2 % | ISO 527 | 5 mm/min |
Flexural modulus | 23.0 °C | 8 GPa Show Material materials with Flexural modulus of 8 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 170 MPa Show Material materials with Flexural strength of 170 MPa | ISO 178 |
Hardness, Ball Indentation | 23.0 °C | 122 MPa Show Material materials with Hardness, Ball Indentation of 122 MPa | ISO 2039-1 |
Hardness, Rockwell R | 23.0 °C | 119 [-] Show Material materials with Hardness, Rockwell R of 119 [-] | ISO 2039-2 |
Impact strength, Charpy notched | -30.0 °C | 6 kJ/m² Show Material materials with Impact strength, Charpy notched of 6 kJ/m² | ISO 179/1eA |
23.0 °C | 7 kJ/m² Show Material materials with Impact strength, Charpy notched of 7 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -30.0 °C | 45 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 45 kJ/m² | ISO 179/1eU |
23.0 °C | 45 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 45 kJ/m² | ISO 179/1eU | |
Impact strength, Izod notched | -30.0 °C | 7 kJ/m² Show Material materials with Impact strength, Izod notched of 7 kJ/m² | ISO 180/1A |
23.0 °C | 8 kJ/m² Show Material materials with Impact strength, Izod notched of 8 kJ/m² | ISO 180/1A | |
Impact strength, Izod unnotched | -30.0 °C | 40 kJ/m² Show Material materials with Impact strength, Izod unnotched of 40 kJ/m² | ISO 180/1U |
23.0 °C | 45 kJ/m² Show Material materials with Impact strength, Izod unnotched of 45 kJ/m² | ISO 180/1U | |
Tensile strength | 23.0 °C | 115 MPa Show Material materials with Tensile strength of 115 MPa | ISO 527 | 5 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2.5E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.5E-5 1/K | ISO 11359-2 | -23°C to 80°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.05E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.05E-4 1/K | ISO 11359-2 | 23°C to 150°C | ||
Heat deflection temperature, 1.80 MPa | 160 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 160 °C | ISO 75/Ae | 1.8 MPa | |||
Relative temperature index, electrical | 125 °C Show Material materials with Relative temperature index, electrical of 125 °C | UL 746B | |||
Relative temperature index, mechanical impact | 110 °C Show Material materials with Relative temperature index, mechanical impact of 110 °C | UL 746B | |||
Relative temperature index, mechanical strength | 125 °C Show Material materials with Relative temperature index, mechanical strength of 125 °C | UL 746B | |||
Vicat softening temperature | 175 °C Show Material materials with Vicat softening temperature of 175 °C | ISO 306 | Rate B/120 | |||
Flammability | UL Recognized, 94HB Flame Class Rating 2nd value | 3mm | UL 94 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 250 V Show Material materials with Comparative tracking index of 250 V | IEC 60112 |
Dielectric constant | 23.0 °C | 3.3 [-] Show Material materials with Dielectric constant of 3.3 [-] | IEC 60250 | at 50/60 Hz |
Dielectric strength | 23.0 °C | 16 kV/mm Show Material materials with Dielectric strength of 16 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
Dissipation factor | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor of 0.01 [-] | IEC 60250 | at 1 MHz |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt volume-flow rate | 8 cm³/10min Show Material materials with Melt volume-flow rate of 8 cm³/10min | ISO 1133 | 250°C/2.16 kg | |
Shrinkage | 23.0 °C | 0.4 - 0.6 % Show Material materials with Shrinkage of 0.4 - 0.6 % | SABIC method |
Shrinkage, transverse | 23.0 °C | 0.5 - 0.9 % Show Material materials with Shrinkage, transverse of 0.5 - 0.9 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Auto Aftermarket,Building Accessory,Circuit Protection,Data Management,Data Transfer,Displays,Doors Hardware/Trim,Electronic Components,Enclosure/Housing/Cover,Enclosures,EV Infrastructure,Forward Lighting,Gas/Electric Oven,Heavy Vehicles,Industrial Material Handling,Infotainment/Telematic,Interior,Lawn/Garden,LED Lighting,Medical Device,Meter Gas,Motorcycle,Personal Care,Photo/Video Camera,Washing Machine,Wireless Communications | |
Fillers | 30% Glass Fiber | |
Processing methods | Drying Temperature: 110-120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-270°C, Nozzle Temperature: 240-260°C, Front - Zone 3 Temperature: 245-265°C, Middle - Zone 2 Temperature: 240-255°C, Rear - Zone 1 Temperature: 230-245°C, Hopper Temperature: 40-60°C, Mold Temperature: 40-100°C |