VALOX™ Resin 735

Want to keep this datasheet? Save it now in your required format

Description

40% glass/mineral, excellent thermal performance/low shrink. Motorized heating appliances, adaptor rings, oven grills, etc. Black/natural only.

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.62 g/cm³

Show Material materials with Density of 1.62 g/cm³

ASTM D 792

Water absorption

23.0 °C

0.07 %

Show Material materials with Water absorption of 0.07 %

ISO 62 | 23°C, 50% RH

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

10.4 GPa

Show Material materials with Elastic modulus of 10.4 GPa

ASTM D 638 | 5 mm/min

Elongation

23.0 °C

2 %

Show Material materials with Elongation of 2 %

ASTM D 638 | Type I, 5 mm/min

Elongation at yield

23.0 °C

2 %

Show Material materials with Elongation at yield of 2 %

ASTM D 638 | Type I, 5 mm/min

Flexural modulus

23.0 °C

8.3 GPa

Show Material materials with Flexural modulus of 8.3 GPa

ISO 178 | 2 mm/min

Flexural strain

23.0 °C

2 %

Show Material materials with Flexural strain of 2 %

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

130 MPa

Show Material materials with Flexural strength of 130 MPa

ISO 178

Flexural yield strength

23.0 °C

130 MPa

Show Material materials with Flexural yield strength of 130 MPa

ISO 178 | 2 mm/min

Hardness, Ball Indentation

23.0 °C

144 MPa

Show Material materials with Hardness, Ball Indentation of 144 MPa

ISO 2039-1

Hardness, Rockwell R

23.0 °C

124 [-]

Show Material materials with Hardness, Rockwell R of 124 [-]

ISO 2039-2

Impact strength, Charpy notched

-30.0 °C

7 kJ/m²

Show Material materials with Impact strength, Charpy notched of 7 kJ/m²

ISO 179/2C

23.0 °C

7 kJ/m²

Show Material materials with Impact strength, Charpy notched of 7 kJ/m²

ISO 179/2C

Impact strength, Charpy unnotched

-30.0 °C

30 kJ/m²

Show Material materials with Impact strength, Charpy unnotched of 30 kJ/m²

ISO 179/1eU

23.0 °C

35 kJ/m²

Show Material materials with Impact strength, Charpy unnotched of 35 kJ/m²

ISO 179/1eU

Unlock all property charts

Impact strength, Izod notched

-30.0 °C

5 kJ/m²

Show Material materials with Impact strength, Izod notched of 5 kJ/m²

ISO 180/1A

23.0 °C

5 kJ/m²

Show Material materials with Impact strength, Izod notched of 5 kJ/m²

ISO 180/1A

Unlock all property charts

Impact strength, Izod notched, ASTM

-30.0 °C

50 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 50 J/m

ASTM D 256

23.0 °C

60 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 60 J/m

ASTM D 256

Unlock all property charts

Impact strength, Izod unnotched

-30.0 °C

25 kJ/m²

Show Material materials with Impact strength, Izod unnotched of 25 kJ/m²

ISO 180/1U

23.0 °C

35 kJ/m²

Show Material materials with Impact strength, Izod unnotched of 35 kJ/m²

ISO 180/1U

Unlock all property charts

Impact strength, Izod unnotched, ASTM

-30.0 °C

520 J/m

Show Material materials with Impact strength, Izod unnotched, ASTM of 520 J/m

ASTM D 4812

23.0 °C

560 J/m

Show Material materials with Impact strength, Izod unnotched, ASTM of 560 J/m

ASTM D 4812

Unlock all property charts

Tensile strength

23.0 °C

95 MPa

Show Material materials with Tensile strength of 95 MPa

ASTM D 638 | Type I, 5 mm/min

Yield strength

23.0 °C

95 MPa

Show Material materials with Yield strength of 95 MPa

ASTM D 638 | Type I, 5 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

2.18E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.18E-5 1/K

ISO 11359-2 | 23°C to 150°C

Coefficient of thermal expansion, transverse

23.0 °C

1.4E-4 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 1.4E-4 1/K

ISO 11359-2 | 23°C to 150°C

Heat deflection temperature, 0.45 MPa

215 °C

Show Material materials with Heat deflection temperature, 0.45 MPa of 215 °C

ISO 75/Bf | 0.45 MPa

Relative temperature index, electrical

140 °C

Show Material materials with Relative temperature index, electrical of 140 °C

UL 746B

Relative temperature index, mechanical impact

140 °C

Show Material materials with Relative temperature index, mechanical impact of 140 °C

UL 746B

Relative temperature index, mechanical strength

140 °C

Show Material materials with Relative temperature index, mechanical strength of 140 °C

UL 746B

Thermal conductivity

23.0 °C

0.36 W/(m·K)

Show Material materials with Thermal conductivity of 0.36 W/(m·K)

ISO 8302

Vicat softening temperature

185 °C

Show Material materials with Vicat softening temperature of 185 °C

ASTM D 1525 | Rate B/50

Flammability

UL Recognized, 94HB Flame Class Rating 2nd value | 3mm | UL 94

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

2 V

Show Material materials with Comparative tracking index of 2 V

UL 746A

Dielectric constant

23.0 °C

3.5 [-]

Show Material materials with Dielectric constant of 3.5 [-]

IEC 60250 | at 50/60 Hz

Dielectric strength

23.0 °C

18 kV/mm

Show Material materials with Dielectric strength of 18 kV/mm

ASTM D 149 | in oil, 3.2 mm

Dissipation factor

23.0 °C

0.02 [-]

Show Material materials with Dissipation factor of 0.02 [-]

IEC 60250 | at 1 MHz

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

20 g/10min

Show Material materials with Melt mass-flow rate of 20 g/10min

ASTM D 1238 | 266°C/5.0 kg

Melt viscosity

260.0 °C

160 Pa·s

Show Material materials with Melt viscosity of 160 Pa·s

ISO 11443 | 1500 sec⁻¹

Melt volume-flow rate

15 cm³/10min

Show Material materials with Melt volume-flow rate of 15 cm³/10min

ISO 1133 | 265°C/5.0 kg

Shrinkage

23.0 °C

0.3 - 0.6 %

Show Material materials with Shrinkage of 0.3 - 0.6 %

SABIC method

Shrinkage, transverse

23.0 °C

0.5 - 0.8 %

Show Material materials with Shrinkage, transverse of 0.5 - 0.8 %

SABIC method

Technological properties

Property
Application areas

Electronic Components,Enclosures,Exterior Mirror,Medical Device,Pump,Wiring Devices

Fillers

40% Glass Fiber and Mineral Powder

Processing methods

Drying Temperature: 110-120°C, Drying Time: 4-6hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 260-285°C, Nozzle Temperature: 265-275°C, Front - Zone 3 Temperature: 260-280°C, Middle - Zone 2 Temperature: 255-280°C, Rear - Zone 1 Temperature: 240-260°C, Hopper Temperature: 40-60°C, Mold Temperature: 60-110°C