XENOY™ Resin 1102

Want to keep this datasheet? Save it now in your required format

Description

Unreinforced PC/polyester alloy. Excellent low temperatue impact/chemical resistance to automotive fluids.

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.19 g/cm³

Show Material materials with Density of 1.19 g/cm³

ASTM D 792

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

150 %

Show Material materials with Elongation of 150 %

ASTM D 638 | Type I, 50 mm/min

Elongation at yield

23.0 °C

4.5 %

Show Material materials with Elongation at yield of 4.5 %

ISO 527 | 50 mm/min

Flexural modulus

23.0 °C

1.87 GPa

Show Material materials with Flexural modulus of 1.87 GPa

ISO 178 | 2 mm/min

Flexural yield strength

23.0 °C

72 MPa

Show Material materials with Flexural yield strength of 72 MPa

ISO 178 | 2 mm/min

Impact strength, Izod notched

-30.0 °C

44 kJ/m²

Show Material materials with Impact strength, Izod notched of 44 kJ/m²

ISO 180/1A

23.0 °C

52 - 54 kJ/m²

Show Material materials with Impact strength, Izod notched of 52 - 54 kJ/m²

ISO 180/1A

Impact strength, Izod notched, ASTM

-30.0 °C

640 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 640 J/m

ASTM D 256

23.0 °C

800 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 800 J/m

ASTM D 256

Unlock all property charts

Tensile strength

23.0 °C

45 MPa

Show Material materials with Tensile strength of 45 MPa

ISO 527 | 50 mm/min

Yield strength

23.0 °C

54 MPa

Show Material materials with Yield strength of 54 MPa

ASTM D 638 | Type I, 50 mm/min

Thermal

PropertyValueComment

Heat deflection temperature, 1.80 MPa

90 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 90 °C

ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed

Rheological Properties

PropertyTemperatureValueComment

Melt volume-flow rate

6 cm³/10min

Show Material materials with Melt volume-flow rate of 6 cm³/10min

ISO 1133 | 250°C/2.16 kg

Shrinkage

23.0 °C

0.8 - 1 %

Show Material materials with Shrinkage of 0.8 - 1 %

SABIC method | 3.2 mm

Shrinkage, transverse

23.0 °C

0.8 - 1 %

Show Material materials with Shrinkage, transverse of 0.8 - 1 %

SABIC method

Technological properties

Property
Application areas

Circuit Protection,City,Door Handle,Electronic Components,Enclosure/Housing/Cover,Enclosures,Energy Management,Exterior Rail Components,Exterior Trim,Heavy Vehicles,Individual Equiptment,LED Lighting,Motorcycle,Non-LED Lighting,Personal Care,Personal Water Craft,Recreational Vehicle,Refrigerator,Vacuum Cleaner

Processing methods

Drying Temperature: 110°C, Drying Time: 4-6hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 260-275°C, Nozzle Temperature: 255-270°C, Front - Zone 3 Temperature: 255-275°C, Middle - Zone 2 Temperature: 250-270°C, Rear - Zone 1 Temperature: 245-265°C, Mold Temperature: 65-90°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 50-80rpm, Shot to Cylinder Size: 50-80%, Vent Depth: 0.013-0.02mm