XENOY™ Resin 1103

Want to keep this datasheet? Save it now in your required format

Description

AUTOMOTIVE. Unreinforced, impact modified PBT+PC alloy. Excellent low temperature impact and chemical resistance. Range gray, black colors.

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.2 g/cm³

Show Material materials with Density of 1.2 g/cm³

ASTM D 792

Water absorption

23.0 °C

0.15 %

Show Material materials with Water absorption of 0.15 %

ISO 62 | 23°C, 50% RH

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

1.89 GPa

Show Material materials with Elastic modulus of 1.89 GPa

ASTM D 638 | 5 mm/min

Elongation

23.0 °C

150 %

Show Material materials with Elongation of 150 %

ASTM D 638 | Type I, 50 mm/min

Elongation at yield

23.0 °C

5 %

Show Material materials with Elongation at yield of 5 %

ASTM D 638 | Type I, 50 mm/min

Flexural modulus

23.0 °C

1.9 GPa

Show Material materials with Flexural modulus of 1.9 GPa

ISO 178 | 2 mm/min

Flexural yield strength

23.0 °C

75 MPa

Show Material materials with Flexural yield strength of 75 MPa

ISO 178 | 2 mm/min

Impact strength, Charpy notched

23.0 °C

57 kJ/m²

Show Material materials with Impact strength, Charpy notched of 57 kJ/m²

ISO 179/1eA

Impact strength, Izod notched

-30.0 °C

42 kJ/m²

Show Material materials with Impact strength, Izod notched of 42 kJ/m²

ISO 180/1A

23.0 °C

50 kJ/m²

Show Material materials with Impact strength, Izod notched of 50 kJ/m²

ISO 180/1A

Impact strength, Izod notched, ASTM

-30.0 °C

530 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 530 J/m

ASTM D 256

23.0 °C

747 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 747 J/m

ASTM D 256

Unlock all property charts

Tensile strength

23.0 °C

50 MPa

Show Material materials with Tensile strength of 50 MPa

ASTM D 638 | Type I, 50 mm/min

Yield strength

23.0 °C

51 MPa

Show Material materials with Yield strength of 51 MPa

ASTM D 638 | Type I, 50 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.71E-4 1/K

Show Material materials with Coefficient of thermal expansion of 1.71E-4 1/K

ASTM E 831 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

2E-4 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 2E-4 1/K

ASTM E 831 | -40°C to 40°C

Heat deflection temperature, 1.80 MPa

87 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 87 °C

ASTM D 648 | 1.82 MPa, 3.2mm, unannealed

Vicat softening temperature

125 °C

Show Material materials with Vicat softening temperature of 125 °C

ASTM D 1525 | Rate B/50

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

13 g/10min

Show Material materials with Melt mass-flow rate of 13 g/10min

ASTM D 1238 | 250°C/5.0 kgf

Melt volume-flow rate

26 cm³/10min

Show Material materials with Melt volume-flow rate of 26 cm³/10min

ISO 1133 | 220°C/5.0 kg

Shrinkage

23.0 °C

0.8 - 1 %

Show Material materials with Shrinkage of 0.8 - 1 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Electronic Components,Enclosure/Housing/Cover,Vacuum Cleaner

Processing methods

Drying Temperature: 110°C, Drying Time: 4-6hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 255-275°C, Nozzle Temperature: 250-265°C, Front - Zone 3 Temperature: 250-270°C, Middle - Zone 2 Temperature: 245-265°C, Rear - Zone 1 Temperature: 240-260°C, Mold Temperature: 40-90°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-80rpm, Shot to Cylinder Size: 50-80%, Vent Depth: 0.013-0.02mm