XENOY™ Resin 1105

Want to keep this datasheet? Save it now in your required format

Description

PBT/PC blend, injection molding grade, non-reinforced, impact modified, excellent toughness at low temperatures, very good paintability

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.2 g/cm³

Show Material materials with Density of 1.2 g/cm³

ASTM D 792

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

1.98 GPa

Show Material materials with Elastic modulus of 1.98 GPa

ASTM D 638 | 5 mm/min

Elongation

23.0 °C

110 %

Show Material materials with Elongation of 110 %

ASTM D 638 | Type I, 5 mm/min

Elongation at yield

23.0 °C

4.1 %

Show Material materials with Elongation at yield of 4.1 %

ASTM D 638 | Type I, 5 mm/min

Flexural modulus

23.0 °C

2.01 GPa

Show Material materials with Flexural modulus of 2.01 GPa

ISO 178 | 2 mm/min

Flexural strain

23.0 °C

7.3 %

Show Material materials with Flexural strain of 7.3 %

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

74 MPa

Show Material materials with Flexural strength of 74 MPa

ASTM D 790 | 1.3 mm/min, 50 mm span

Flexural yield strength

23.0 °C

78 MPa

Show Material materials with Flexural yield strength of 78 MPa

ISO 178 | 2 mm/min

Hardness, Shore D

23.0 °C

79 [-]

Show Material materials with Hardness, Shore D of 79 [-]

ISO 868

Impact strength, Charpy notched

-30.0 °C

47 kJ/m²

Show Material materials with Impact strength, Charpy notched of 47 kJ/m²

ISO 179/1eA

23.0 °C

62 kJ/m²

Show Material materials with Impact strength, Charpy notched of 62 kJ/m²

ISO 179/1eA

Impact strength, Izod notched

-40.0 °C

34 kJ/m²

Show Material materials with Impact strength, Izod notched of 34 kJ/m²

ISO 180/1A

-30.0 °C

51 kJ/m²

Show Material materials with Impact strength, Izod notched of 51 kJ/m²

ISO 180/1A

23.0 °C

63 kJ/m²

Show Material materials with Impact strength, Izod notched of 63 kJ/m²

ISO 180/1A

Unlock all property charts

Impact strength, Izod notched, ASTM

-40.0 °C

372 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 372 J/m

ASTM D 256

-30.0 °C

489 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 489 J/m

ASTM D 256

-20.0 °C

687 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 687 J/m

ASTM D 256

-10.0 °C

695 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 695 J/m

ASTM D 256

23.0 °C

755 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 755 J/m

ASTM D 256

Unlock all property charts

Tensile strength

23.0 °C

46 MPa

Show Material materials with Tensile strength of 46 MPa

ASTM D 638 | Type I, 5 mm/min

Yield strength

23.0 °C

45 MPa

Show Material materials with Yield strength of 45 MPa

ASTM D 638 | Type I, 5 mm/min

Thermal

PropertyValueComment

Heat deflection temperature, 0.45 MPa

109 °C

Show Material materials with Heat deflection temperature, 0.45 MPa of 109 °C

ISO 75/Bf | 0.45 MPa

Vicat softening temperature

122 °C

Show Material materials with Vicat softening temperature of 122 °C

ASTM D 1525 | Rate B/50

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

16 g/10min

Show Material materials with Melt mass-flow rate of 16 g/10min

ISO 1133 | 250°C/5 kg

Shrinkage

23.0 °C

0.8 - 1 %

Show Material materials with Shrinkage of 0.8 - 1 %

SABIC method | 3.2 mm

Shrinkage, transverse

23.0 °C

0.8 - 1 %

Show Material materials with Shrinkage, transverse of 0.8 - 1 %

SABIC method

Technological properties

Property
Application areas

Spoiler

Processing methods

Drying Temperature: 110°C, Drying Time: 4-6hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 260-275°C, Nozzle Temperature: 255-270°C, Front - Zone 3 Temperature: 255-275°C, Middle - Zone 2 Temperature: 250-270°C, Rear - Zone 1 Temperature: 245-265°C, Mold Temperature: 65-90°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 50-80rpm, Shot to Cylinder Size: 50-80%, Vent Depth: 0.013-0.02mm