General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 1.22 g/cm³ Show Material materials with Density of 1.22 g/cm³ | ASTM D 792 |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongation | 23.0 °C | 120 % Show Material materials with Elongation of 120 % | ASTM D 638 | Type I, 50 mm/min |
Flexural modulus | 23.0 °C | 2.34 GPa Show Material materials with Flexural modulus of 2.34 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Flexural yield strength | 23.0 °C | 93 MPa Show Material materials with Flexural yield strength of 93 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Impact strength, Izod notched, ASTM | -30.0 °C | 106 J/m Show Material materials with Impact strength, Izod notched, ASTM of 106 J/m | ASTM D 256 |
23.0 °C | 160 - 667 J/m Show Material materials with Impact strength, Izod notched, ASTM of 160 - 667 J/m | ASTM D 256 | |
Yield strength | 23.0 °C | 61 MPa Show Material materials with Yield strength of 61 MPa | ASTM D 638 | Type I, 50 mm/min |
Thermal
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 8.28E-5 1/K Show Material materials with Coefficient of thermal expansion of 8.28E-5 1/K | ASTM E 831 | -40°C to 95°C | ||
Heat deflection temperature, 1.80 MPa | 107 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 107 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed | |||
Relative temperature index, electrical | 75 °C Show Material materials with Relative temperature index, electrical of 75 °C | UL 746B | |||
Relative temperature index, mechanical impact | 75 °C Show Material materials with Relative temperature index, mechanical impact of 75 °C | UL 746B | |||
Relative temperature index, mechanical strength | 75 °C Show Material materials with Relative temperature index, mechanical strength of 75 °C | UL 746B | |||
Flammability | UL Recognized, 94HB Flame Class Rating | 1.49mm | UL 94 | ||||
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Comparative tracking index | 23.0 °C | 2 V Show Material materials with Comparative tracking index of 2 V | UL 746A |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Shrinkage | 23.0 °C | 0.5 - 0.7 % Show Material materials with Shrinkage of 0.5 - 0.7 % | SABIC method | 3.2 mm |
Shrinkage, transverse | 23.0 °C | 0.6 - 0.8 % Show Material materials with Shrinkage, transverse of 0.6 - 0.8 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Building Accessory,Circuit Protection,Cooking Range,Data Transfer,Displays,Door Handle,Doors Hardware/Trim,Electronic Components,Enclosures,Energy Management,Exterior Mirror,Exterior Trim,Front Grille,Heavy Vehicles,Lawn/Garden,Medical Device,Medical Facility Infrastructure,Meter Water,Motorcycle,Personal Computing,Photo/Video Camera,Photovoltaic Components,Power Boat,Refrigerator,Swimming Pool/Spa,Watch/Jewelry,Water Treatment/Filtration,Wearables,Wheel Cover,Wireless Communications,Wiring Devices | |
| Processing methods | Drying Temperature: 110°C, Drying Time: 4-6hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 260-275°C, Nozzle Temperature: 255-270°C, Front - Zone 3 Temperature: 255-275°C, Middle - Zone 2 Temperature: 250-270°C, Rear - Zone 1 Temperature: 245-265°C, Mold Temperature: 65-90°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 50-80rpm, Shot to Cylinder Size: 50-80%, Vent Depth: 0.013-0.02mm | |