General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.05 g/cm³ Show Material materials with Density of 1.05 g/cm³ | ASTM D 792 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.97 GPa Show Material materials with Elastic modulus of 2.97 GPa | ASTM D 638 | 50 mm/min |
Elongation | 23.0 °C | 20.5 % Show Material materials with Elongation of 20.5 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 5 % Show Material materials with Elongation at yield of 5 % | ASTM D 638 | Type I, 50 mm/min |
Flexural modulus | 23.0 °C | 3.17 GPa Show Material materials with Flexural modulus of 3.17 GPa | ISO 178 | 2 mm/min, 64mm |
Hardness, Shore D | 23.0 °C | 74 [-] Show Material materials with Hardness, Shore D of 74 [-] | ISO 868 |
Impact strength, Charpy notched | -30.0 °C | 1 kJ/m² Show Material materials with Impact strength, Charpy notched of 1 kJ/m² | ISO 179/1eA |
23.0 °C | 2 kJ/m² Show Material materials with Impact strength, Charpy notched of 2 kJ/m² | ISO 179/1eA | |
Impact strength, Izod notched | -30.0 °C | 1 kJ/m² Show Material materials with Impact strength, Izod notched of 1 kJ/m² | ISO 180/1A |
23.0 °C | 2 kJ/m² Show Material materials with Impact strength, Izod notched of 2 kJ/m² | ISO 180/1A | |
Impact strength, Izod notched, ASTM | 23.0 °C | 21 J/m Show Material materials with Impact strength, Izod notched, ASTM of 21 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 410 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 410 J/m | ASTM D 4812 | 23°C, 63.5*12.7*3.2mm, Cut |
Tensile strength | 23.0 °C | 29 MPa Show Material materials with Tensile strength of 29 MPa | ASTM D 638 | Type I, 50 mm/min |
Yield strength | 23.0 °C | 36 MPa Show Material materials with Yield strength of 36 MPa | ASTM D 638 | Type I, 50 mm/min |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 5.8E-5 1/K Show Material materials with Coefficient of thermal expansion of 5.8E-5 1/K | ISO 11359-2 | -30°C to 100°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 1.15E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.15E-4 1/K | ISO 11359-2 | -30°C to 100°C |
Heat deflection temperature, 1.80 MPa | 73 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 73 °C | ASTM D 648 | 1.82 MPa, 3.2 mm | |
Vicat softening temperature | 157 °C Show Material materials with Vicat softening temperature of 157 °C | ISO 306 | 10N, 50°C/hr |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 18 g/10min Show Material materials with Melt mass-flow rate of 18 g/10min | ISO 1133 | 230°C/2.16 kg | |
Shrinkage | 23.0 °C | 0.95 % Show Material materials with Shrinkage of 0.95 % | SABIC method | 48 hrs @ 23°C |
Shrinkage, transverse | 23.0 °C | 1.25 % Show Material materials with Shrinkage, transverse of 1.25 % | SABIC method | 48 hrs @ 23°C |
Technological properties
Property | ||
---|---|---|
Application areas | Interior | |
Fillers | Talc | |
Processing methods | Drying Temperature: 80-100°C, Drying Time: 2-4hrs, Melt Temperature: 210-270°C, Nozzle Temperature: 210-270°C, Front - Zone 3 Temperature: 210-270°C, Middle - Zone 2 Temperature: 200-250°C, Rear - Zone 1 Temperature: 190-230°C, Mold Temperature: 15-60°C, Back Pressure: 1-1.5MPa |