Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 1.67 g/cm³ Show Material materials with Density of 1.67 g/cm³ | ASTM D 792 |
Water absorption | 23.0 °C | 0.07 % Show Material materials with Water absorption of 0.07 % | ISO 62 | 23°C, 50% RH |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 11.5 GPa Show Material materials with Elastic modulus of 11.5 GPa | ASTM D 638 | 5 mm/min |
Elongation | 23.0 °C | 2 % Show Material materials with Elongation of 2 % | ASTM D 638 | Type I, 5 mm/min |
Elongation at yield | 23.0 °C | 2 % Show Material materials with Elongation at yield of 2 % | ASTM D 638 | Type I, 5 mm/min |
Flexural modulus | 23.0 °C | 9.6 GPa Show Material materials with Flexural modulus of 9.6 GPa | ISO 178 | 2 mm/min |
Flexural strain | 23.0 °C | 3 % Show Material materials with Flexural strain of 3 % | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 200 MPa Show Material materials with Flexural strength of 200 MPa | ISO 178 |
Flexural yield strength | 23.0 °C | 200 MPa Show Material materials with Flexural yield strength of 200 MPa | ISO 178 | 2 mm/min |
Hardness, Ball Indentation | 23.0 °C | 115 MPa Show Material materials with Hardness, Ball Indentation of 115 MPa | ISO 2039-1 |
Hardness, Rockwell R | 23.0 °C | 118 [-] Show Material materials with Hardness, Rockwell R of 118 [-] | ISO 2039-2 |
Impact strength, Charpy notched | -30.0 °C | 9 kJ/m² Show Material materials with Impact strength, Charpy notched of 9 kJ/m² | ISO 179/2C |
23.0 °C | 11 kJ/m² Show Material materials with Impact strength, Charpy notched of 11 kJ/m² | ISO 179/2C | |
Impact strength, Charpy unnotched | -30.0 °C | 55 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 55 kJ/m² | ISO 179/1eU |
23.0 °C | 50 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 50 kJ/m² | ISO 179/1eU | |
Impact strength, Izod notched | -30.0 °C | 8 kJ/m² Show Material materials with Impact strength, Izod notched of 8 kJ/m² | ISO 180/1A |
23.0 °C | 8 kJ/m² Show Material materials with Impact strength, Izod notched of 8 kJ/m² | ISO 180/1A | |
Impact strength, Izod notched, ASTM | -30.0 °C | 80 J/m Show Material materials with Impact strength, Izod notched, ASTM of 80 J/m | ASTM D 256 |
23.0 °C | 80 J/m Show Material materials with Impact strength, Izod notched, ASTM of 80 J/m | ASTM D 256 | |
Impact strength, Izod unnotched | -30.0 °C | 45 kJ/m² Show Material materials with Impact strength, Izod unnotched of 45 kJ/m² | ISO 180/1U |
23.0 °C | 45 kJ/m² Show Material materials with Impact strength, Izod unnotched of 45 kJ/m² | ISO 180/1U | |
Impact strength, Izod unnotched, ASTM | -30.0 °C | 660 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 660 J/m | ASTM D 4812 |
23.0 °C | 660 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 660 J/m | ASTM D 4812 | |
Tensile strength | 23.0 °C | 130 MPa Show Material materials with Tensile strength of 130 MPa | ASTM D 638 | Type I, 5 mm/min |
Yield strength | 23.0 °C | 130 MPa Show Material materials with Yield strength of 130 MPa | ASTM D 638 | Type I, 5 mm/min |
Thermal
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.4E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.4E-5 1/K | ISO 11359-2 | 23°C to 150°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.3E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.3E-4 1/K | ISO 11359-2 | 23°C to 150°C | ||
Heat deflection temperature, 0.45 MPa | 220 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 220 °C | ISO 75/Bf | 0.45 MPa | |||
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | |||
Relative temperature index, mechanical impact | 130 °C Show Material materials with Relative temperature index, mechanical impact of 130 °C | UL 746B | |||
Relative temperature index, mechanical strength | 140 °C Show Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | |||
Vicat softening temperature | 205 °C Show Material materials with Vicat softening temperature of 205 °C | ASTM D 1525 | Rate B/50 | |||
Flammability | UL Recognized, 94V-0 Flame Class Rating | 0.75mm | UL 94 | ||||
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Comparative tracking index | 23.0 °C | 250 V Show Material materials with Comparative tracking index of 250 V | IEC 60112 |
Dielectric constant | 23.0 °C | 3.5 [-] Show Material materials with Dielectric constant of 3.5 [-] | ASTM D 150 | at 1 MHz |
Dielectric strength | 23.0 °C | 19 kV/mm Show Material materials with Dielectric strength of 19 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
Dissipation factor | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor of 0.01 [-] | ASTM D 150 | at 1 MHz |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt mass-flow rate | 90 g/10min Show Material materials with Melt mass-flow rate of 90 g/10min | ASTM D 1238 | 266°C/5.0 kg | |
Melt viscosity | 260.0 °C | 115 Pa·s Show Material materials with Melt viscosity of 115 Pa·s | ISO 11443 | 1500 sec⁻¹ |
Melt volume-flow rate | 65 cm³/10min Show Material materials with Melt volume-flow rate of 65 cm³/10min | ISO 1133 | 265°C/5.0 kg | |
Shrinkage | 23.0 °C | 0.1 - 0.3 % Show Material materials with Shrinkage of 0.1 - 0.3 % | SABIC method |
Shrinkage, transverse | 23.0 °C | 0.4 - 0.7 % Show Material materials with Shrinkage, transverse of 0.4 - 0.7 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Circuit Protection,Electronic Components,Enclosure/Housing/Cover,Enclosures,HVAC Underhood,Personal Computing,Pump,Vending Machine,Washing Machine,Wiring Devices | |
| Fillers | 30% Glass Fiber | |
| Processing methods | Drying Temperature: 110-120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-270°C, Nozzle Temperature: 240-260°C, Front - Zone 3 Temperature: 245-265°C, Middle - Zone 2 Temperature: 240-255°C, Rear - Zone 1 Temperature: 230-245°C, Hopper Temperature: 40-60°C, Mold Temperature: 40-100°C | |