SABIC® PPcompound 7727

Want to keep this datasheet? Save it now in your required format

Description

SABIC® PPcompound 7727 is a mineral filled, impact modified polypropylene TPO. This material combines impact resistance, heat stability, and is used in injection molded applications. IMDS ID: 209708556

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1 g/cm³ Show Material materials with Density of 1 g/cm³	ASTM D 792

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	1.96 GPa Show Material materials with Elastic modulus of 1.96 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	26.7 % Show Material materials with Elongation of 26.7 %	ISO 527 \| 50 mm/min
Elongation at yield	23.0 °C	4.6 % Show Material materials with Elongation at yield of 4.6 %	ISO 527 \| 50 mm/min
Flexural modulus	23.0 °C	2.05 GPa Show Material materials with Flexural modulus of 2.05 GPa	ISO 178 \| 2 mm/min, 64mm
Impact strength, Charpy notched	23.0 °C	4 kJ/m² Show Material materials with Impact strength, Charpy notched of 4 kJ/m²	ISO 179/1eA
Tensile strength	23.0 °C	18 MPa Show Material materials with Tensile strength of 18 MPa	ISO 527 \| 50 mm/min, 1A
Yield strength	23.0 °C	25 MPa Show Material materials with Yield strength of 25 MPa	ISO 527 \| 50 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	5.6E-5 1/K Show Material materials with Coefficient of thermal expansion of 5.6E-5 1/K	ISO 11359-2 \| -30°C to 100°C
Coefficient of thermal expansion, transverse	23.0 °C	1.16E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.16E-4 1/K	ISO 11359-2 \| -30°C to 100°C
Heat deflection temperature, 1.80 MPa		62 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 62 °C	ISO 75-1&2 \| 1.8 MPa

Rheological Properties

Property	Value	Comment
Melt mass-flow rate	23 g/10min Show Material materials with Melt mass-flow rate of 23 g/10min	ISO 1133 \| 230°C/2.16 kg

Technological properties

Property
Application areas	Load Floor
Fillers	Mineral Powder
Processing methods	Drying Temperature: 80-100°C, Drying Time: 2-4hrs, Melt Temperature: 210-270°C, Nozzle Temperature: 210-270°C, Front - Zone 3 Temperature: 210-270°C, Middle - Zone 2 Temperature: 200-250°C, Rear - Zone 1 Temperature: 190-230°C, Mold Temperature: 15-60°C, Back Pressure: 1-1.5MPa