General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.02 g/cm³ Show Material materials with Density of 1.02 g/cm³ | ASTM D 792 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.78 GPa Show Material materials with Elastic modulus of 2.78 GPa | ASTM D 638 | 50 mm/min |
Elongation | 23.0 °C | 22 % Show Material materials with Elongation of 22 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 5 % Show Material materials with Elongation at yield of 5 % | ASTM D 638 | Type I, 50 mm/min |
Flexural modulus | 23.0 °C | 2.22 GPa Show Material materials with Flexural modulus of 2.22 GPa | ISO 178 | 2 mm/min, 64mm |
Hardness, Shore D | 23.0 °C | 66 [-] Show Material materials with Hardness, Shore D of 66 [-] | ISO 868 |
Impact strength, Charpy notched | -30.0 °C | 2 kJ/m² Show Material materials with Impact strength, Charpy notched of 2 kJ/m² | ISO 179/1eA |
23.0 °C | 6 kJ/m² Show Material materials with Impact strength, Charpy notched of 6 kJ/m² | ISO 179/1eA | |
Impact strength, Izod notched | -30.0 °C | 2 kJ/m² Show Material materials with Impact strength, Izod notched of 2 kJ/m² | ISO 180/1A |
23.0 °C | 4 kJ/m² Show Material materials with Impact strength, Izod notched of 4 kJ/m² | ISO 180/1A | |
Impact strength, Izod notched, ASTM | 23.0 °C | 45 J/m Show Material materials with Impact strength, Izod notched, ASTM of 45 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 1080 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 1080 J/m | ASTM D 4812 | 23°C, 63.5*12.7*3.2mm, Cut |
Tensile strength | 23.0 °C | 20 MPa Show Material materials with Tensile strength of 20 MPa | ASTM D 638 | Type I, 50 mm/min |
Yield strength | 23.0 °C | 27 MPa Show Material materials with Yield strength of 27 MPa | ASTM D 638 | Type I, 50 mm/min |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 7E-6 1/K Show Material materials with Coefficient of thermal expansion of 7E-6 1/K | ISO 11359-2 | -30°C to 100°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 1.8E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.8E-5 1/K | ISO 11359-2 | -30°C to 100°C |
Heat deflection temperature, 1.80 MPa | 60 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 60 °C | ASTM D 648 | 1.82 MPa, 3.2 mm | |
Vicat softening temperature | 144 °C Show Material materials with Vicat softening temperature of 144 °C | ISO 306 | 10N, 50°C/hr |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 21 g/10min Show Material materials with Melt mass-flow rate of 21 g/10min | ISO 1133 | 230°C/2.16 kg | |
Shrinkage | 23.0 °C | 1 % Show Material materials with Shrinkage of 1 % | SABIC method | 1 Hour, 80°C |
Shrinkage, transverse | 23.0 °C | 1.4 % Show Material materials with Shrinkage, transverse of 1.4 % | SABIC method | 1 Hour, 80°C |
Technological properties
Property | ||
---|---|---|
Application areas | Overhead | |
Fillers | Mineral Powder | |
Processing methods | Drying Temperature: 80-100°C, Drying Time: 2-4hrs, Melt Temperature: 210-270°C, Nozzle Temperature: 210-270°C, Front - Zone 3 Temperature: 210-270°C, Middle - Zone 2 Temperature: 200-250°C, Rear - Zone 1 Temperature: 190-230°C, Mold Temperature: 15-60°C, Back Pressure: 1-1.5MPa |