SABIC® COHERE™ 8102

Want to keep this datasheet? Save it now in your required format

Description

SABIC® COHERE™ 8102 is an ethylene-octene copolymers produced via solution polymerization using metallocene catalyst. It performs well in high performance LLDPE blown film applications with an excellent combination of toughness, hot tack, sealing and optical properties.

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

0.9 g/cm³

Show Material materials with Density of 0.9 g/cm³

ASTM D1505

Mooney viscosity

23.0 °C

20 MU

Show Material materials with Mooney viscosity of 20 MU

ASTM D1646 | ML 1+4, 121 °C

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

800 %

Show Material materials with Elongation of 800 %

ASTM D638

Flexural modulus

23.0 °C

0.08 GPa

Show Material materials with Flexural modulus of 0.08 GPa

ASTM D790

Tensile strength

23.0 °C

24.5 MPa

Show Material materials with Tensile strength of 24.5 MPa

ASTM D638

Thermal

PropertyValueComment

Glass transition temperature

-31 °C

Show Material materials with Glass transition temperature of -31 °C

SABIC method

Melting point

98 °C

Show Material materials with Melting point of 98 °C

SABIC method

Optical

PropertyValueComment

Haze

4 %

Show Material materials with Haze of 4 %

ASTM D1003

Technological properties

Property
Application areas

General purpose film,Lamination film